Aromatic amine compound, and light-emitting element, light-emitting device, and electronic appliance using the aromatic amine compound

ABSTRACT

An object of the present invention is to provide a novel aromatic amine compound, and a light-emitting element, a light-emitting device, and an electronic appliance with high luminous efficiency. An aromatic amine compound expressed by General Formula (1) and a light-emitting element, a light-emitting device, and an electronic appliance formed using the aromatic amine compound expressed by General Formula (1) are provided. By the use of the aromatic amine compound expressed by General Formula (1), the light-emitting element, the light-emitting device, and the electronic appliance can have high luminous efficiency.

BACKGROUND OF THE INVENTION

1. Field of Invention

The present invention relates to an aromatic amine compound, and alight-emitting element, a light-emitting device, and an electronicappliance each using the aromatic amine compound.

2. Description of the Related Art

In recent years, research and development have been extensivelyconducted on a light-emitting element using a compound with alight-emitting property. In a basic structure of such a light-emittingelement, a layer containing an organic compound with a light-emittingproperty is sandwiched between a pair of electrodes. By application ofvoltage to this element, electrons and holes are injected from the pairof electrodes to the layer containing an organic compound with alight-emitting property to cause current flow. Then, by recombination ofthese carriers (electrons and holes), the organic compound with alight-emitting property forms an excited state, and light is emittedwhen the excited state returns to a ground state. Because of such amechanism, this kind of light-emitting element is called alight-emitting element of current excitation type.

A great advantage of such a light-emitting element lies in its thinnessand lightness in weight because the light-emitting element is formed by,for example, an organic thin film with a thickness of about 0.1 μm.Moreover, another advantage thereof is high response speed because thetime it takes for light emission after carrier injection is about 1 μsor shorter. In view of these advantages, it is considered that thelight-emitting element is suitable for a flat panel display element.

Since the light-emitting element is formed into a film shape, surfacelight emission can be easily obtained by forming a large-area element.This is a feature which is difficult to be obtained in point lightsources typified by an incandescent lamp and an LED or line lightsources typified by a fluorescent lamp. Accordingly, the utility valueof the light-emitting element is also high as a surface light sourceapplicable to illumination and the like.

In order to overcome many problems derived from materials of such alight-emitting element and to improve its element characteristics,improvement of an element structure, material development, and so on arecarried out.

For example, Nonpatent Document 1 describes a light-emitting elementusing a blue light-emitting material.

[Nonpatent Document 1] Meng-Huan Ho, Yao-Shan Wu and Chin H. Chen, 2005SID International Symposium Digest of Technical Papers, p 802-805SUMMARY OF THE INVENTION

In a light-emitting element described in Nonpatent Document 1,4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (NPB) is used for a layerwhich is in contact with a light-emitting layer. However, NPB has lowsinglet-excitation energy and the energy may transfer from alight-emitting material in an excited state. In particular, in a case ofa light-emitting material for emitting blue light, which has a shortwavelength, the energy is more likely to transfer to NPB because of ahigh energy level in an excited state. The energy transfer to NPB causesa problem of decrease in luminous efficiency of a light-emittingelement.

Therefore, it is an object of the present invention to provide a novelaromatic amine compound.

It is another object of the present invention to provide alight-emitting element, a light-emitting device, and an electronicappliance each having high luminous efficiency.

An aspect of the present invention is an aromatic amine compoundexpressed by General Formula (1).

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; and Ar¹ represents an aryl group having 6 to 25 carbon atoms.Moreover, α represents a substituent expressed by any of GeneralFormulae (1-1) to (1-4). In General Formulae (1-1) to (1-4), R¹¹ and R¹²each represent any of a hydrogen atom, an alkyl group having 1 to 4carbon atoms, and an aryl group having 6 to 12 carbon atoms; and R¹³ toR¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent a hydrogenatom or an alkyl group having 1 to 4 carbon atoms.)

Among the aromatic amine compounds that can be expressed by GeneralFormula (1), an aromatic amine compound expressed by General Formula (3)is preferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and Ar¹ represents an aryl group having 6 to 25 carbonatoms. Moreover, α represents a substituent expressed by any of GeneralFormulae (3-1) to (3-4). In General Formulae (3-1) to (3-4), R¹¹ and R¹²each represent any of a hydrogen atom, an alkyl group having 1 to 4carbon atoms, and an aryl group having 6 to 12 carbon atoms; and R¹³ toR¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent a hydrogenatom or an alkyl group having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (5) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and R³ to R⁷ each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and a phenyl group. Moreover, αrepresents a substituent expressed by any of General Formulae (5-1) to(5-4). In General Formulae (5-1) to (5-4), R¹¹ and R¹² each representany of a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, andan aryl group having 6 to 12 carbon atoms; and R¹³ to R¹⁹, R²¹ to R²⁹,R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent a hydrogen atom or an alkylgroup having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (7) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, α represents a substituent expressed by any ofGeneral Formulae (7-1) to (7-4). In General Formulae (7-1) to (7-4), R¹¹and R¹² each represent any of a hydrogen atom, an alkyl group having 1to 4 carbon atoms, and an aryl group having 6 to 12 carbon atoms; andR¹³ to R¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent ahydrogen atom or an alkyl group having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (9) or (10) ispreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, R¹¹ and R¹² each represent any of a hydrogenatom, an alkyl group having 1 to 4 carbon atoms, and an aryl grouphaving 6 to 12 carbon atoms.)

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, R³⁰ represents a hydrogen atom or an alkyl grouphaving 1 to 4 carbon atoms.)

An aspect of the present invention is an aromatic amine compoundexpressed by General Formula (2).

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; and Ar¹ represents an aryl group having 6 to 25 carbon atoms.Moreover, α represents a substituent expressed by either of GeneralFormulae (2-1) and (2-2). In General Formulae (2-1) and (2-2), R⁵¹ andR⁵² each represent any of a hydrogen atom, an alkyl group having 1 to 4carbon atoms, and an aryl group having 6 to 12 carbon atoms; and R⁵³ toR⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogen atom or an alkyl grouphaving 1 to 4 carbon atoms.)

Among the aromatic amine compounds that can be expressed by GeneralFormula (2), an aromatic amine compound expressed by General Formula (4)is preferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and Ar¹ represents an aryl group having 6 to 25 carbonatoms. Moreover, α represents a substituent expressed by either ofGeneral Formulae (4-1) and (4-2). In General Formulae (4-1) and (4-2),R⁵¹ and R⁵² each represent any of a hydrogen atom, an alkyl group having1 to 4 carbon atoms, and an aryl group having 6 to 12 carbon atoms; andR⁵³ to R⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogen atom or an alkylgroup having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (6) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and R³ to R⁷ each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and a phenyl group. Moreover, αrepresents a substituent expressed by either of General Formulae (6-1)and (6-2). In General Formulae (6-1) and (6-2), R⁵¹ and R⁵² eachrepresent any of a hydrogen atom, an alkyl group having 1 to 4 carbonatoms, and an aryl group having 6 to 12 carbon atoms; and R⁵³ to R⁵⁸ andR⁶¹ to R⁶⁸ each represent a hydrogen atom or an alkyl group having 1 to4 carbon atoms.)

An aromatic amine compound expressed by General Formula (8) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, α represents a substituent expressed by eitherof General Formulae (8-1) and (8-2). In General Formulae (8-1) and(8-2), R⁵¹ and R⁵² each represent any of a hydrogen atom, an alkyl grouphaving 1 to 4 carbon atoms, and an aryl group having 6 to 12 carbonatoms; and R⁵³ to R⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogen atom oran alkyl group having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (11) or (12) ismore preferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, R⁵¹ and R⁵² each represent any of a hydrogenatom, an alkyl group having 1 to 4 carbon atoms, and an aryl grouphaving 6 to 12 carbon atoms.)

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms.)

An aspect of the present invention is a light-emitting element havingthe aforementioned aromatic amine compound between a pair of electrodes.

An aspect of the present invention is a light-emitting element includinga light-emitting layer and a layer containing the aforementionedaromatic amine compound between a pair of electrodes. In thelight-emitting element, the layer containing the aromatic amine compoundis in contact with the light-emitting layer.

An aspect of the present invention is a light-emitting element includinga light-emitting layer and the aforementioned aromatic amine compoundbetween a pair of electrodes, in which the aromatic amine compound isincluded in the light-emitting layer.

In the above structure, the light-emitting layer includes aphosphorescent material which emits phosphorescent light. In particular,an advantageous effect of the present invention can be obtained more ina case of including a phosphorescent material which emits green light.

In the above structure, the light-emitting layer includes a fluorescentmaterial which emits fluorescent light. In particular, an advantageouseffect of the present invention can be obtained more in a case ofincluding a fluorescent material which emits blue light.

Moreover, a light-emitting device of the present invention has alight-emitting element including the aforementioned aromatic aminecompound and a controller for controlling light emission of thelight-emitting element. It is to be noted that the light-emitting devicein this specification includes an image display device, a light-emittingdevice, and a light source (including an illumination apparatus).Further, the light-emitting device includes a module in which aconnector such as an FPC (Flexible Printed Circuit), a TAB (TapeAutomated Bonding) tape, or a TCP (Tape Carrier Package) is attached toa panel, a module in which a print wiring board is provided at an end ofa TAB tape or an TCP, and a module in which an IC (Integrated Circuit)is directly mounted on a light-emitting device by a COG (Chip On Glass)method.

An electronic appliance using the light-emitting element of the presentinvention in its display portion is also included in the category of thepresent invention. Therefore, an electronic appliance of the presentinvention has a display portion provided with the aforementionedlight-emitting element and a controller for controlling light emissionof the light-emitting element.

The aromatic amine compound of the present invention has a wide band gapand can be used for a layer which is in contact with a light-emittingmaterial, and moreover can be used as a material for dispersing alight-emitting material. When the aromatic amine compound of the presentinvention is provided in contact with a light-emitting material, thetransfer of excitation energy of the light-emitting material can beprevented and the luminous efficiency can be improved. Further, even ifthe aromatic amine compound of the present invention is excited, theenergy can transfer from the aromatic amine compound of the presentinvention to the light-emitting material; therefore, the luminousefficiency can be improved.

With the aromatic amine compound of the present invention used for alight-emitting element, a light-emitting device, and an electronicappliance, the light-emitting element, the light-emitting device, andthe electronic appliance can have high luminous efficiency.

BRIEF DESCRIPTION OF THE DRAWINGS

In the accompanying drawings:

FIGS. 1A to 1C explain light-emitting elements of the present invention;

FIG. 2 explains a light-emitting element of the present invention;

FIGS. 3A and 3B explain a light-emitting device of the presentinvention;

FIG. 4 explains a light-emitting device of the present invention;

FIGS. 5A to 5D explain electronic appliances of the present invention;

FIG. 6 explains an electronic appliance of the present invention;

FIG. 7 explains a light-emitting device of the present invention;

FIG. 8 explains light-emitting devices of the present invention;

FIG. 9 explains a light-emitting element of the present invention;

FIGS. 10A and 10B each show a ¹H-NMR chart of9-[4-(N-phenylamino)phenyl]carbazole;

FIGS. 11A and 11B each show a ¹H-NMR chart ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIG. 12 shows a DSC chart ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIG. 13 shows an absorption spectrum of a toluene solution ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIG. 14 shows an absorption spectrum of a thin film ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIG. 15 shows a light emission spectrum of a toluene solution ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIG. 16 shows a light emission spectrum of a thin film ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIG. 17 shows a CV measurement result ofN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine;

FIGS. 18A and 18B each show a ¹H-NMR chart of4-(carbazol-9-yl)phenyl-4′-phenyltriphenylamine;

FIG. 19 shows a DSC chart of4-(carbazol-9-yl)phenyl-4′-phenyltriphenylamine;

FIG. 20 shows a light emission spectrum of a toluene solution of4-(carbazol-9-yl)phenyl-4′-phenyltriphenylamine;

FIGS. 21A and 21B each show a ¹H-NMR chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIG. 22 shows a DSC chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIG. 23 shows an absorption spectrum of a toluene solution ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIG. 24 shows an absorption spectrum of a thin film ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIG. 25 shows a light emission spectrum of a toluene solution ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIG. 26 shows a light emission spectrum of a thin film ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIG. 27 shows a CV measurement result ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine;

FIGS. 28A and 28B each show a ¹H-NMR chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 29 shows a DSC chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 30 shows an absorption spectrum of a toluene solution ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 31 shows an absorption spectrum of a thin film ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 32 shows a light emission spectrum of a toluene solution ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 33 shows a light emission spectrum of a thin film ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 34 shows a CV measurement result ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-4,4′-biphenyl-diamine;

FIG. 35 explains a light-emitting element of Embodiment 5.

FIG. 36 shows current density-luminance characteristics of alight-emitting element manufactured in accordance with Embodiment 5;

FIG. 37 shows voltage-luminance characteristics of a light-emittingelement manufactured in accordance with Embodiment 5;

FIG. 38 shows luminance-current efficiency characteristics of alight-emitting element manufactured in accordance with Embodiment 5;

FIG. 39 shows current density-luminance characteristics of alight-emitting element manufactured in accordance with Embodiment 6;

FIG. 40 shows voltage-luminance characteristics of a light-emittingelement manufactured in accordance with Embodiment 6;

FIG. 41 shows luminance-current efficiency characteristics of alight-emitting element manufactured in accordance with Embodiment 6;

FIG. 42 shows triplet-excitation energy of an aromatic amine compound ofthe present invention;

FIGS. 43A and 43B each show a ¹H-NMR chart of2-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-5-phenyl-1,3,4-oxadiazole;

FIGS. 44A and 44B each show a ¹H-NMR chart of9-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-10-phenylanthracene;

FIG. 45 shows a ¹H-NMR chart of9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene;

FIGS. 46A and 46B each show a ¹H-NMR chart of4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP);

FIG. 47 shows an absorption spectrum of a toluene solution of4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP);

FIG. 48 shows an absorption spectrum of a thin film of4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP);

FIG. 49 shows a light emission spectrum of a toluene solution of4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP);

FIG. 50 shows a light emission spectrum of a thin film of4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP);

FIGS. 51A and 51B each show a ¹H-NMR chart of4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP);

FIG. 52 shows an absorption spectrum of a toluene solution of4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP);

FIG. 53 shows an absorption spectrum of a thin film of4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP);

FIG. 54 shows a light emission spectrum of a toluene solution of4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP);

FIG. 55 shows a light emission spectrum of a thin film of4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP);

FIGS. 56A and 56B each show a ¹H-NMR chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP);

FIGS. 57A and 57B each show a ¹³C-NMR chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP);

FIG. 58 shows an absorption spectrum ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP);

FIG. 59 shows a light emission spectrum ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP);

FIGS. 60A and 60B each show a ¹H-NMR chart of9-(4-bromo-1-naphthyl)carbazole;

FIGS. 61A and 61B each show a ¹H-NMR chart ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP);

FIG. 62 shows an absorption spectrum ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP);

FIG. 63 shows a light emission spectrum ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP);

FIGS. 64A and 64B each show a ¹H-NMR chart ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-di-1-naphthylbiphenyl-4,4′-diamine(abbr.: CNNBP);

FIG. 65 shows an absorption spectrum ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-di-1-naphthylbiphenyl-4,4′-diamine(abbr.: CNNBP);

FIG. 66 shows a light emission spectrum ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-di-1-naphthylbiphenyl-4,4′-diamine(abbr.: CNNBP);

FIG. 67 explains a light-emitting element of Embodiment 12;

FIG. 68 shows current density-luminance characteristics of alight-emitting element manufactured in accordance with Embodiment 12;

FIG. 69 shows voltage-luminance characteristics of a light-emittingelement manufactured in accordance with Embodiment 12;

FIG. 70 shows luminance-current efficiency characteristics of alight-emitting element manufactured in accordance with Embodiment 12;

FIG. 71 shows a light emission spectrum of a light-emitting elementmanufactured in accordance with Embodiment 12;

FIG. 72 shows a DSC chart ofN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di-(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP);

FIG. 73 shows a DSC chart ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP); and

FIG. 74 shows a DSC chart ofN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-di-1-naphthylbiphenyl-4,4′-diamine(abbr.: CNNBP).

DETAILED DESCRIPTION OF THE INVENTION

Embodiment modes and embodiments of the present invention will behereinafter described with reference to the drawings. However, thepresent invention is not limited to the following description and it iseasily understood by those skilled in the art that the mode and detailcan be variously changed without departing from the scope and spirit ofthe present invention. Therefore, the present invention is not construedas being limited to the description of the embodiment modes andembodiments hereinafter shown.

Embodiment Mode 1

Embodiment Mode 1 will explain an aromatic amine compound of the presentinvention.

An aromatic amine compound of the present invention is an aromatic aminecompound expressed by General Formula (1).

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; and Ar¹ represents an aryl group having 6 to 25 carbon atoms.Moreover, α represents a substituent expressed by any of GeneralFormulae (1-1) to (1-4). In General Formulae (1-1) to (1-4), R¹¹ and R¹²each represent any of a hydrogen atom, an alkyl group having 1 to 4carbon atoms, and an aryl group having 6 to 12 carbon atoms; and R¹³ toR¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent a hydrogenatom or an alkyl group having 1 to 4 carbon atoms.)

In General Formula (1), R¹ and R² each represent a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Specifically, a substituent shown by any of StructureFormulae (13-1) to (13-12) is given.

In General Formula (1), A¹ represents an arylene group having 6 to 25carbon atoms. Specifically, a substituent shown by any of StructureFormulae (14-1) to (14-6) is given.

In General Formula (1), Ar¹ represents an aryl group having 6 to 25carbon atoms. Specifically, a substituent shown by any of StructureFormulae (15-1) to (15-6) is given.

Among the aromatic amine compounds that can be expressed by GeneralFormula (1), an aromatic amine compound expressed by General Formula (3)is preferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and Ar¹ represents an aryl group having 6 to 25 carbonatoms. Moreover, α represents a substituent expressed by any of GeneralFormulae (3-1) to (3-4). In General Formulae (3-1) to (3-4), R¹¹ and R¹²each represent any of a hydrogen atom, an alkyl group having 1 to 4carbon atoms, and an aryl group having 6 to 12 carbon atoms; and R¹³ toR¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent a hydrogenatom or an alkyl group having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (5) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and R³ to R⁷ each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and a phenyl group. Moreover, αrepresents a substituent expressed by any of General Formulae (5-1) to(5-4). In General Formulae (5-1) to (5-4), R¹¹ and R¹² each representany of a hydrogen atom, an alkyl group having 1 to 4 carbon atoms, andan aryl group having 6 to 12 carbon atoms; and R¹³ to R¹⁹, R²¹ to R²⁹,R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent a hydrogen atom or an alkylgroup having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (7) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, α represents a substituent expressed by any ofGeneral Formulae (7-1) to (7-4). In General Formulae (7-1) to (7-4), R¹¹and R¹² each represent any of a hydrogen atom, an alkyl group having 1to 4 carbon atoms, and an aryl group having 6 to 12 carbon atoms; andR¹³ to R¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent ahydrogen atom or an alkyl group having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (9) or (10) ispreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and R¹¹ and R¹² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 12carbon atoms.)

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and R³⁰ represents a hydrogen atom or an alkyl grouphaving 1 to 4 carbon atoms.)

An aromatic amine compound of the present invention is an aromatic aminecompound expressed by General Formula (2).

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; and Ar¹ represents an aryl group having 6 to 25 carbon atoms.Moreover, α represents a substituent expressed by either of GeneralFormulae (2-1) and (2-2). In General Formulae (2-1) and (2-2), R⁵¹ andR⁵² each represent any of a hydrogen atom, an alkyl group having 1 to 4carbon atoms, and an aryl group having 6 to 12 carbon atoms; and R⁵³ toR⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogen atom or an alkyl grouphaving 1 to 4 carbon atoms.)

In General Formula (2), R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms. Specifically, a substituent shown by any of StructureFormulae (13-1) to (13-12) is given.

In General Formula (2), A¹ represents any of an arylene group having 6to 25 carbon atoms. Specifically, a substituent shown by any ofStructure Formulae (14-1) to (14-6) is given.

In General Formula (2), Ar¹ represents any of an aryl group having 6 to25 carbon atoms. Specifically, a substituent shown by any of StructureFormulae (15-1) to (15-6) is given.

Among the aromatic amine compounds expressed by General Formula (2), anaromatic amine compound expressed by General Formula (4) is preferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and Ar¹ represents an aryl group having 6 to 25 carbonatoms. Moreover, α represents a substituent expressed by either ofGeneral Formulae (4-1) and (4-2). In General Formulae (4-1) and (4-2),R⁵¹ and R⁵² each represent any of a hydrogen atom, an alkyl group having1 to 4 carbon atoms, and an aryl group having 6 to 12 carbon atoms; andR⁵³ to R⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogen atom or an alkylgroup having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (6) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; and R³ to R⁷ each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and a phenyl group. Moreover, αrepresents a substituent expressed by either of General Formulae (6-1)and (6-2). In General Formulae (6-1) and (6-2), R⁵¹ and R⁵² eachrepresent any of a hydrogen atom, an alkyl group having 1 to 4 carbonatoms, and an aryl group having 6 to 12 carbon atoms; and R⁵³ to R⁵⁸ andR⁶¹ to R⁶⁸ each represent a hydrogen atom or an alkyl group having 1 to4 carbon atoms.)

An aromatic amine compound expressed by General Formula (8) is morepreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, α represents a substituent expressed by eitherof General Formulae (8-1) and (8-2). In General Formulae (8-1) and(8-2), R⁵¹ and R⁵² each represent any of a hydrogen atom, an alkyl grouphaving 1 to 4 carbon atoms, and an aryl group having 6 to 12 carbonatoms; and R⁵³ to R⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogen atom oran alkyl group having 1 to 4 carbon atoms.)

An aromatic amine compound expressed by General Formula (11) or (12) ispreferable.

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms. Moreover, R⁵¹ and R⁵² each represent any of a hydrogenatom, an alkyl group having 1 to 4 carbon atoms, and an aryl grouphaving 6 to 12 carbon atoms.)

(In the formula, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms.)

As a specific example of the aromatic amine compound of the presentinvention, an aromatic amine compound expressed by any of StructureFormulae (21) to (119) is given. However, the present invention is notlimited to these.

The aromatic amine compound of the present invention expressed byGeneral Formula (1) can be synthesized by a synthesizing methodexpressed by Synthesis

First, a compound (Compound A) including carbazole in its skeleton isreacted with a dihalide of an aromatic compound by a coupling reactionusing a metal catalyst to synthesize a compound (Compound B) includingN-(arylhalide)carbazole in its skeleton; then, a coupling reaction witharylamine is carried out using a metal catalyst such as palladium toobtain Compound C. In Synthesis Scheme (A-1), a halogen element (X¹, X²)of the dihalide of the aromatic compound is preferably iodine orbromine. Moreover, X¹ and X² may be either the same or different. Eachof R¹ and R² represents any of a hydrogen atom, an alkyl group having 1to 4 carbon atoms, and an aryl group having 6 to 25 carbon atoms. Thearomatic amine compound is preferably a compound having 6 to 25 carbonatoms. The arylamine preferably has 6 to 25 carbon atoms.

Compound C can be reacted with a halide of a fluorene derivative or ahalide of a biphenyl derivative by a coupling reaction using a palladiumcatalyst or an Ullmann reaction using copper, thereby synthesizing thearomatic amine compound of the present invention.

In Synthesis Schemes (B-1) to (B-4), X¹ to X⁴ each represent a halogenatom. In addition, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; and Ar¹ represents an aryl group having 6 to 25 carbon atoms.Moreover, R¹¹ and R¹² each represent any of a hydrogen atom, an alkylgroup having 1 to 4 carbon atoms, and an aryl group having 6 to 12carbon atoms. R¹³ to R¹⁹, R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ eachrepresent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms.

In Synthesis Schemes (B-1) to (B-4), a compound expressed by GeneralFormula (1-1a) corresponds to a case where α in the aforementionedGeneral Formula (1) is General Formula (1-1), a compound expressed byGeneral Formula (1-2a) corresponds to a case where at in theaforementioned General Formula (1) is General Formula (1-2), a compoundexpressed by General Formula (1-3a) corresponds to a case where α in theaforementioned General Formula (1) is General Formula (1-3), and acompound expressed by General Formula (1-4a) corresponds to a case whereα in the aforementioned General Formula (1) is General Formula (1-4).

In Synthesis Scheme (B-1), the compound expressed by General Formula(1-1a) can be synthesized by coupling a halide of a fluorene derivativeand Compound C in accordance with a coupling reaction using a palladiumcatalyst or an Ullumann reaction using copper. A halogen element of thehalide of the fluorene derivative is preferably iodine or bromine.

Similarly, in Synthesis Schemes (B-2) to (B-4), the compounds expressedby General Formulae (1-2a) to (1-4a) can be synthesized by coupling ahalide of a biphenyl derivative and Compound C in accordance with acoupling reaction using a palladium catalyst or an Ullumann reactionusing copper. A halogen element of the halide of the biphenyl derivativeis preferably iodine or bromine.

Moreover, the aromatic amine compound of the present invention expressedby General Formula (2) can be synthesized by a synthesizing methodexpressed by Synthesis Schemes (B-5) and (B-6).

In Synthesis Schemes (B-5) and (B-6), X⁵ to X⁸ each represent a halogenatom. Moreover, R¹ and R² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 25carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; and Ar¹ represents an aryl group having 6 to 25 carbon atoms. Inaddition, R⁵¹ and R⁵² each represent any of a hydrogen atom, an alkylgroup having 1 to 4 carbon atoms, and an aryl group having 6 to 12carbon atoms; and R⁵³ to R⁵⁸ and R⁶¹ to R⁶⁸ each represent a hydrogenatom or an alkyl group having 1 to 4 carbon atoms.

In Synthesis Schemes (B-5) and (B-6), a compound expressed by GeneralFormula (2-1a) corresponds to a case where a in the aforementionedGeneral Formula (2) is General Formula (2-1), and a compound expressedby General Formula (2-2a) corresponds to a case where a in theaforementioned General Formula (2) is General Formula (2-2).

In Synthesis Scheme (B-5), the compound expressed by General Formula(2-1a) can be synthesized by coupling a halide of a fluorene derivativeand Compound C in accordance with a coupling reaction using a palladiumcatalyst or an Ullumann reaction using copper. A halogen element of thehalide of the fluorene derivative is preferably iodine or bromine.

Similarly, in Synthesis Scheme (B-6), the compound expressed by GeneralFormula (2-2a) can be synthesized by coupling a halide of a biphenylderivative and Compound C in accordance with a coupling reaction using apalladium catalyst or an Ullumann reaction using copper. A halogenelement of the halide of the biphenyl derivative is preferably iodine orbromine.

Moreover, in Synthesis Schemes (B-5) and (B-6), the aromatic aminecompound of the present invention of General Formula (2) can be obtainedthrough one-stage reaction by reacting two equivalents of Compound Cwith respect to the halide.

In the above-described synthetic schemes, tri(tert-butyl)phosphine((tert-Bu)₃P) can be used as a ligand for the coupling reaction using apalladium catalyst. As the Pd catalyst, a catalyst in which (tert-Bu)₃Pis coordinated in bis(dibenzylideneacetone)palladium(0) (abbr.:Pd(dba)₂) by mixing bis(dibenzylideneacetone)palladium(0) and(tert-Bu)₃P can be used. It is to be noted that other ligands than(tert-Bu)₃P may be used as the ligand in the case of using the palladiumcatalyst. For example, DPPF can be used besides (tert-Bu)₃P. As thepalladium catalyst, Pd(dba)₂, palladium diacetate (Pd(OAc)₂), or thelike can be used. Preferably, Pd(dba)₂ is used. The reaction temperatureis preferably in the range of room temperature to 130° C. It is morepreferable to set the heating temperature in the range from 60° C. to110° C. Note that dba refers to trans,trans-dibenzylideneacetone. Inaddition, DPPF refers to 1,1-bis(diphenylphosphino)ferrocene. As asolvent, toluene, xylene, or the like can be used. As a base, alkalimetal alkoxide such as tert-BuONa; potassium carbonate (K₂CO₃); or thelike can be used.

Since the aromatic amine compound of the present invention has a wideband gap, the aromatic amine compound can be used as a host material ofa light-emitting material which emits light with a short wavelength, andmoreover used for a layer which is in contact with a light-emittingmaterial which emits light with a short wavelength.

More specifically, the aromatic amine compound of the present inventionis effectively used as a host material for a fluorescent material whichemits fluorescent light with a short wavelength, such as blue light, andmoreover, effectively used for a layer which is in contact with a layercontaining a fluorescent material which emits fluorescent light with ashort wavelength because of the following reason. Since the aromaticamine compound of the present invention has high triplet level andsinglet level, the energy transfer from an excited fluorescent materialto the aromatic amine compound of the present invention does not easilyoccur. Therefore, the excited energy of the fluorescent material can beextracted efficiently as light emission. In addition, when the aromaticamine compound of the present invention is excited, the energy transferfrom the triplet level or the singlet level of the excited aromaticamine compound to the fluorescent material becomes possible and theluminous efficiency of the light-emitting element can be improved. Inthe case of using the aromatic amine compound of the present inventionfor a layer which is in contact with a layer containing a fluorescentmaterial, it is more effective to provide a light-emitting region closeto a layer containing the aromatic amine compound of the presentinvention. In a case of a fluorescent material which emits light with alonger wavelength, the use of the aromatic amine compound of the presentinvention can offer a similar advantageous effect.

Specifically, the aromatic amine compound of the present invention iseffectively used as a host material for a phosphorescent material whichemits phosphorescent light with a relatively short wavelength such asgreen light, and moreover, effectively used for a layer which is incontact with a layer containing a phosphorescent material which emitsphosphorescent light with a relatively short wavelength because of thefollowing reason. Since the aromatic amine compound of the presentinvention has a high triplet level, the energy transfer from an excitedphosphorescent material to the aromatic amine compound of the presentinvention does not easily occur. Therefore, the excited energy of thephosphorescent material can be extracted efficiently as light emission.In addition, when the aromatic amine compound of the present inventionis excited, the energy transfer from the triplet level of the excitedaromatic amine compound to the triplet level of the phosphorescentmaterial becomes possible and the luminous efficiency of thelight-emitting element can be improved. In the case of using thearomatic amine compound of the present invention for a layer which is incontact with a layer containing a phosphorescent material, it is moreeffective to provide a light-emitting region close to a layer containingthe aromatic amine compound of the present invention. In a case of aphosphorescent material which emits light with a longer wavelength, theuse of the aromatic amine compound of the present invention can offer asimilar advantageous effect.

In particular, among the aromatic amine compounds of the presentinvention, the aromatic amine compound expressed by General Formula (1)with an asymmetrical structure is preferable because the band gap iswider and the triplet level is also high.

Moreover, the aromatic amine compound of the present invention issuperior in a hole-transporting property; therefore, the aromatic aminecompound can be used for a hole-transporting layer of a light-emittingelement, thereby providing the light-emitting element with favorablecharacteristics.

Moreover, the aromatic amine compound expressed by General Formula (2)is superior in heat resistance. Therefore, by the use of the aromaticamine compound expressed by General Formula (2), a device superior inheat resistance can be obtained.

Embodiment Mode 2

An aspect of a light-emitting element using an aromatic amine compoundof the present invention will be hereinafter described with reference toFIG. 1A.

A light-emitting element of the present invention has a plurality oflayers between a pair of electrodes. The plurality of layers are formedby stacking a layer containing a substance with a high carrier-injectingproperty and a layer containing a substance with a highcarrier-transporting property so that a light-emitting region is formedapart from the electrodes, i.e., so that carrier recombination iscarried out in a portion apart from the electrodes.

In this embodiment mode, the light-emitting element includes a firstelectrode 102; a first layer 103, a second layer 104, a third layer 105,and a fourth layer 106 which are stacked in this order over the firstelectrode 102; and a second electrode 107 provided over them. In theexplanation of this embodiment mode, the first electrode 102 functionsas an anode and the second electrode 107 functions as a cathode.

The substrate 101 is used as a support for the light-emitting element.As the substrate 101, for example, a glass substrate, a plasticsubstrate, or the like can be used. Other substrates than these can alsobe used as long as the substrate functions as a support during amanufacturing process of the light-emitting element.

The first electrode 102 is preferably formed of a metal, alloy,conductive compound, mixture of these, or the like each having a highwork function (specifically, 4.0 eV or higher). Specifically, forexample, indium oxide-tin oxide (ITO: Indium Tin Oxide), indiumoxide-tin oxide including silicon or silicon oxide, indium oxide-zincoxide (IZO: Indium Zinc Oxide), indium oxide including tungsten oxideand zinc oxide (IWZO), or the like is given. Films of these conductivemetal oxides are usually formed by sputtering; however, a sol-gel methodor the like may also be used. For example, indium oxide-zinc oxide (IZO)can be formed by a sputtering method using a target in which 1 to 20 wt% of zinc oxide with respect to indium oxide is included. Moreover,indium oxide (IWZO) including tungsten oxide and zinc oxide can beformed by a sputtering method using a target in which 0.5 to 5 wt % oftungsten oxide and 0.1 to 1 wt % of zinc oxide with respect to indiumoxide are included. In addition, gold (Au), platinum (Pt), nickel (Ni),tungsten (W), chromium (Cr), molybdenum (Mo), iron (Fe), cobalt (Co),copper (Cu), palladium (Pd), a nitride of a metal material (such astitanium nitride (TiN)), or the like is given.

The first layer 103 includes a substance with a high hole-injectingproperty and can be formed of molybdenum oxide (MoO_(x)), vanadium oxide(VO_(x)), ruthenium oxide (RuO_(x)), tungsten oxide (WO_(x)), manganeseoxide (MnO_(x)), or the like. In addition, phthalocyanine (abbr.: H₂PC),a phthalocyanine-based compound such as copper phthalocyanine (CuPC), ahigh-molecular material such aspoly(ethylenedioxythiophene)/poly(styrenesulfonate) (PEDOT/PSS), or thelike can also be used to form the first layer 103.

Moreover, the first layer 103 can be formed of a composite materialincluding an organic compound and an inorganic compound. In particular,in a composite material including an organic compound and an inorganiccompound exhibiting an electron-accepting property with respect to theorganic compound, electrons are transported between the organic compoundand the inorganic compound to increase carrier density; thus, thehole-injecting property and the hole-transporting property areexcellent.

When the first layer 103 is formed of a composite material including anorganic compound and an inorganic compound, since ohmic contact with thefirst electrode 102 becomes possible, the material for the firstelectrode can be selected regardless of its work function.

The inorganic compound used for the composite material is preferably anoxide of a transition metal. Moreover, an oxide of a metal belonging toany of Groups 4 to 8 in the periodic table can be used. Specifically,vanadium oxide, niobium oxide, tantalum oxide, chromium oxide,molybdenum oxide, tungsten oxide, manganese oxide, and rhenium oxide arepreferable for their high electron-accepting property. Above all,molybdenum oxide is preferable because it is stable even in the air, ithas a low moisture-absorption property, and it is easily handled.

The organic compound used for the composite material can be variouskinds of compounds including an aromatic amine compound, a carbazolederivative, aromatic hydrocarbon, a high-molecular compound (such asoligomer, dendrimer, or polymer), and so on. The organic compound usedfor the composite material preferably has a high hole-transportingproperty. Specifically, a substance having a hole mobility of 10⁻⁶cm²/Vs or higher is preferable. However, other materials than these canalso be used as long as the hole-transporting property is higher thanthe electron-transporting property. The organic compound which can beused for the composite material will hereinafter be describedspecifically.

For example, the aromatic amine compound may beN,N′-di(p-tolyl)-N,N′-diphenyl-p-phenylenediamine (abbr.: DTDPPA);4,4′-bis[N-(4-diphenylaminophenyl)-N-phenylamino]biphenyl (abbr.: DPAB);4,4′-bis(N-{4-[N-(3-methylphenyl)-N-phenylamino]phenyl}-N-phenylamino)biphenyl(abbr.: DNTPD);1,3,5-tris[N-(4-diphenylaminophenyl)-N-phenylamino]benzene (abbr.:DPA3B); or the like.

As the carbazole derivative which can be used for the compositematerial, specifically, the following can be given:3-[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole (abbr.:PCzPCA1);3,6-bis[N-(9-phenylcarbazol-3-yl)-N-phenylamino]-9-phenylcarbazole(abbr.: PCzPCA2);3-[N-(1-naphthyl)-N-(9-phenylcarbazol-3-yl)amino]-9-phenylcarbazole(abbr.: PCzPCN1); or the like.

Moreover, 4,4′-di(N-carbazolyl)biphenyl (abbr.: CBP);1,3,5-tris[4-(N-carbazolyl)phenyl]benzene (abbr.: TCPB);9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbr.: CZPA);1,4-bis[4-(N-carbazolyl)phenyl-2,3,5,6-tetraphenylbenzene; or the likecan be used.

As the aromatic hydrocarbon which can be used for the compositematerial, for example, the following can be given:2-tert-butyl-9,10-di(2-naphthyl)anthracene (abbr.: t-BuDNA);2-tert-butyl-9,10-di(1-naphthyl)anthracene;9,10-bis(3,5-diphenylphenyl)anthracene (abbr.: DPPA);2-tert-butyl-9,10-bis(4-phenylphenyl)anthracene (abbr.: t-BuDBA);9,10-di(2-naphthyl)anthracene (abbr.: DNA); 9,10-diphenylanthracene(abbr.: DPAnth); 2-tert-butylanthracene (abbr.: t-BuAnth);9,10-bis(4-methyl-1-naphthyl)anthracene (abbr.: DMNA);2-tert-butyl-9,10-bis[2-(1-naphthyl)phenyl]anthracene;9,10-bis[2-(1-naphthyl)phenyl]anthracene;2,3,6,7-tetramethyl-9,10-di(1-naphthyl)anthracene;2,3,6,7-tetramethyl-9,10-di(2-naphthyl)anthracene; 9,9′-bianthryl;10,10′-diphenyl-9,9′-bianthryl;10,10′-bis(2-phenylphenyl)-9,9′-bianthryl;10,10′-bis[(2,3,4,5,6-pentaphenyl)phenyl]-9,9′-bianthryl; anthracene;tetracene; rubrene; perylene; 2,5,8,11-tetra(tert-butyl)perylene; or thelike. In addition to these, pentacene, coronene, or the like can also beused. In this way, the aromatic hydrocarbon having a hole mobility of1×10⁻⁶ cm²/Vs or higher and 14 to 42 carbon atoms is more preferablyused.

The aromatic hydrocarbon which can be used for the composite materialmay have a vinyl skeleton. As the aromatic hydrocarbon having a vinylgroup, for example, 4,4′-bis(2,2-diphenylvinyl)biphenyl (abbr.: DPVBi);9,10-bis[4-(2,2-diphenylvinyl)phenyl]anthracene (abbr.: DPVPA); or thelike is given.

In addition, a high-molecular compound such as poly(N-vinylcarbazole)(abbr.: PVK) or poly(4-vinyltriphenylamine) (abbr.: PVTPA) can be used.

The second layer 104 includes a substance with a high hole-transportingproperty. The aromatic amine compound of the present invention shown inEmbodiment Mode 1 can be suitably used for the second layer 104 for itsexcellent hole-transporting property. When the aromatic amine compoundof the present invention is used for the second layer 104, alight-emitting element with favorable characteristics can be obtained.

The third layer 105 is a layer containing a substance with alight-emitting property. The substance with a light-emitting property isnot particularly limited and various kinds of materials can be used. Forexample, as a fluorescent material which emits fluorescent light, thefollowing can be given: coumarin derivatives such as coumarin 6 andcoumarin 545T; quinacridone derivatives such asN,N′-dimethylquinacridone and N,N′-diphenylquinacridone; acridonederivatives such as N-phenylacridone and N-methylacridone; condensedaromatic compounds such as 2-tert-butyl-9,10-di(2-naphthyl)anthracene(abbr.: t-BuDNA), 9,10-diphenylanthracene (abbr.: DPhA), rubrene,periflanthene, and 2,5,8,11-tetra(tert-butyl)perylene (abbr.: TBP);pyran derivatives such as4-dicyanomethylene-2-[p-(dimethylamino)styryl]-6-methyl-4H-pyran; aminederivatives such as 4-(2,2-diphenylvinyl)triphenylamine,9-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-10-phenylanthracene(abbr.: YGAPA); and so on. As a phosphorescent material which emitsphosphorescent light, the following can be given: iridium complexes suchas tris(2-phenylpyridinato)iridium(III) (abbr.: Ir(ppy)₃),bis(2-phenylpyridinato)iridium(III)acetylacetonate (abbr.:Ir(ppy)₂(acac)), bis{2-p-tolyl)pyridinato}iridium(III)acetylacetonate(abbr.: Ir(tpy)₂(acac)),bis{2-(2′-benzothienyl)pyridinato}iridium(III)acetylacetonate (abbr.:Ir(btp)₂(acac)), andbis{2-(4,6-difluorophenyl)pyridinato}iridium(III)picolinate (abbr.:FIrpic); platinum complexes such as a2,3,7,8,12,13,17,18-octaethyl-21H,23H-porphyrin-platinum complex(pt(OEP)); rare-earth complexes such as4,7-diphenyl-1,10-phenanthrolinetris(2-tenoyltrifluoroacetonato)europium(III);and the like.

The present invention is effective when the substance with alight-emitting property included in the third layer 105 is a materialwhich emits blue fluorescent light. Specifically, a fluorescent materialwhich emits blue light, such as the aforementioned t-BuDNA, DPhA, TBP,or YGAPA, is preferably used.

Moreover, the present invention is effective when the substance with alight-emitting property included in the third layer 105 is a substancewhich emits green phosphorescent light. Specifically, a phosphorescentmaterial which emits green light, such as the aforementioned Ir(ppy)₃,Ir(ppy)₂(acac), or Ir(tpy)₂(acac), or a phosphorescent material whichemits blue-green light such as the aforementioned FIrpic is preferablyused.

The third layer 105 may be formed by dispersing the aforementionedsubstance with a light-emitting property. As a material for dispersingthe substance with a light-emitting property, various kinds of materialscan be used. In particular, a substance with a higher LUMO level and alower HOMO level than the substance with a light-emitting property ispreferable. Specifically, the following can be used:4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (abbr.: NPB),tris(8-quinolinolato)aluminum (abbr.: Alq),bis(2-methyl-8-quinolinolato)(4-phenylphenolato)aluminum (abbr.: BAlq),bis[2-(2-hydroxyphenyl)benzoxazolato]zinc (abbr.:Zn(BOX)₂),2-tert-butyl-9,10-di(2-naphthyl)anthracene (abbr.: t-BuDNA),9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbr.: CzPA),2-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-5-phenyl-1,3,4-oxadiazole(abbr.: YGAO11), and the like. Moreover, plural kinds of materials maybe employed to disperse the substance with a light-emitting property.For example, a substance which suppresses crystallization, such asrubrene, may be further added to suppress crystallization. In addition,NPB, Alq, or the like may be further added in order to transfer energyto the substance with a light-emitting property more efficiently.

The fourth layer 106 can be formed of a substance with a highelectron-transporting property. For example, the fourth layer 106includes the following metal complex having a quinoline skeleton or abenzoquinoline skeleton, or the like: tris(8-quinolinolato)aluminum(abbr.: Alq); tris(4-methyl-8-quinolinolato)aluminum (abbr.: Almq₃);bis(10-hydroxybenzo[h]-quinolinato)beryllium (abbr.: BeBq₂);bis(2-methyl-8-quinolinolato)(4-phenylphenolato)aluminum (BAlq); and thelike. Besides those, the following metal complex having an oxazole-basedligand or a thiazole-based ligand, or the like can be used:bis[2-(2-hydroxyphenyl)benzoxazolato]zinc (abbreviation: Zn(BOX)₂);bis[2-(2-hydroxyphenyl)benzothiazolato]zinc (abbreviation: Zn(BTZ)₂);and the like. Furthermore, in addition to the metal complex,2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (abbreviation:PBD); 1,3-bis[5-(p-tert-butylphenyl)-1,3,4-oxadiazole-2-yl]benzene(abbreviation: OXD-7);3-(4-biphenylyl)-4-phenyl-5-(4-tert-butylphenyl)-1,2,4-triazole(abbreviation: TAZ); bathophenanthroline (abbreviation: BPhen);bathocuproin (abbreviation: BCP); and the like can also be used. Thesubstances mentioned here mainly have an electron mobility of 10⁻⁶cm²/Vs or higher. It is to be noted that the electron-transporting layermay include a substance other than those above as long as the substancehas a higher electron-transporting property than hole-transportingproperty. Moreover, the electron-transporting layer may have not only asingle-layer structure but also a stacked-layer structure including twoor more layers formed of the above-mentioned substances.

The second electrode 107 can be formed of a metal, alloy, electricallyconductive compound, or mixture of these, each having a low workfunction (specifically, 3.8 eV or lower). As a typical example of acathode material, an element belonging to Group 1 or 2 in the periodictable, i.e., an alkali metal such as lithium (Li) or cesium (Cs), or analkaline earth metal such as magnesium (Mg), calcium (Ca), or strontium(Sr); an alloy containing any of these (such as MgAg or AlLi); a rareearth metal such as europium (Er) or ytterbium (Yb); an alloy containinga rare earth metal; or the like can be used. However, when a layerhaving a function of promoting electron injection is provided betweenthe second electrode 107 and the fourth layer 106 as a stack with thesecond electrode, the second electrode 107 can be formed of variousconductive materials such as Al, Ag, ITO, or ITO including siliconregardless of its work function.

For the layer having a function of promoting electron injection, analkali metal, an alkaline earth metal, or a compound of an alkali metalor an alkaline earth metal, such as lithium fluoride (LiF), cesiumfluoride (CsF), or calcium fluoride (CaF₂) can be used. For example, alayer which includes a substance with an electron-transporting propertyand also includes an alkali metal, an alkaline earth metal, or acompound of an alkali metal or an alkaline earth metal can be used.Specifically, for example, Alq including magnesium (Mg), or the like canbe used. It is to be noted that as the electron-injecting layer, analkali metal or an alkaline earth metal is preferably included in thelayer which includes a substance with an electron-transporting propertybecause electron injection from the second electrode 107 is efficientlyperformed.

The first layer 103, the second layer 104, the third layer 105, and thefourth layer 106 can be formed by not only an evaporation method butalso various methods such as an ink jet method or a spin coating method.Moreover, a different forming method may be used for each electrode oreach layer.

In the light-emitting element of the present invention having theaforementioned structure, current flows by a potential differencegenerated between the first electrode 102 and the second electrode 107and holes and electrons are recombined in the third layer 105, which isthe layer containing a substance with a high light-emitting property;thus, light is emitted. In other words, in this structure, alight-emitting region is formed in the third layer 105.

The emitted light is extracted to the outside through one or both of thefirst electrode 102 and the second electrode 107. Therefore, one or bothof the first electrode 102 and the second electrode 107 is/are formed ofa substance with a light-transmitting property. When only the firstelectrode 102 is formed of a substance with a light-transmittingproperty, the emitted light is extracted from the substrate side throughthe first electrode 102 as shown in FIG. 1A. Meanwhile, when only thesecond electrode 107 is formed of a substance with a light-transmittingproperty, the emitted light is extracted from the side opposite to thesubstrate side through the second electrode 107 as shown in FIG. 1B.When each of the first electrode 102 and the second electrode 107 isformed of a substance with a light-transmitting property, the emittedlight is extracted from both the substrate side and the side opposite tothe substrate side through the first electrode 102 and the secondelectrode 107 as shown in FIG. 1C.

The structure of the layers provided between the first electrode 102 andthe second electrode 107 is not limited to the aforementioned one. Astructure other than the aforementioned one may also be used as long asa light-emitting region in which holes and electrons are recombined isprovided in a portion apart from the first electrode 102 and the secondelectrode 107 so that light disappearance caused by approximationbetween the light-emitting region and metal is suppressed.

That is to say, the stacked-layer structure is not particularly limited,and layers containing a substance with a high electron-transportingproperty, a substance with a high hole-transporting property, asubstance with a high electron-injecting property, a substance with ahigh hole-injecting property, a substance with a bipolar property (amaterial with a high electron and hole transporting property), asubstance with a hole-blocking property, and the like may be freelycombined with the aromatic amine compound of the present invention.

In a structure of the light-emitting element shown in FIG. 2, a firstlayer 303 containing a substance with a high electron-transportingproperty, a second layer 304 containing a substance with alight-emitting property, a third layer 305 containing a substance with ahigh hole-transporting property, a fourth layer 306 containing asubstance with a high hole-injecting property, and a second electrode307 functioning as an anode are stacked in this order over a firstelectrode 302 functioning as a cathode. It is to be noted that referencenumeral 301 denotes a substrate.

In this embodiment mode, the light-emitting element is manufactured overa substrate made of glass, plastic, or the like. When a plurality ofsuch light-emitting elements are manufactured over one substrate, apassive light-emitting device can be manufactured. Moreover, forexample, a thin film transistor (TFT) may be formed over a substratemade of glass, plastic, or the like so that a light-emitting element ismanufactured over an electrode electrically connected to the TFT. Thus,an active matrix light-emitting device in which driving of thelight-emitting element is controlled by the TFT can be manufactured. Thestructure of the TFT is not particularly limited. The TFT may be eithera staggered type or an inverted staggered type. The crystallinity of asemiconductor used for the TFT is not limited in particular, and thesemiconductor may be either amorphous or crystalline. Moreover, a drivercircuit formed over the TFT substrate may include N-type and P-type TFTsor only one of N-type and P type TFTs.

Since the aromatic amine compound of the present invention has a wideband gap, a light-emitting element with the use of the aromatic aminecompound of the present invention can have favorable characteristics.

The aromatic amine compound of the present invention is effectively usedfor a layer which is in contact with a layer containing a fluorescentmaterial which emits fluorescent light with a short wavelength becauseof the following reason. Since the aromatic amine compound of thepresent invention has high triplet level and singlet level, the energytransfer from an excited fluorescent material to the aromatic aminecompound of the present invention does not easily occur. Therefore, theexcited energy of the fluorescent material can be extracted efficientlyas light emission. In addition, when the aromatic amine compound of thepresent invention is excited, the energy transfer from the triplet levelor the singlet level of the excited aromatic amine compound to thefluorescent material becomes possible and the luminous efficiency of thelight-emitting element can be improved. In the case of using thearomatic amine compound of the present invention for a layer which is incontact with a layer containing a fluorescent material, it is moreeffective to provide a light-emitting region close to a layer containingthe aromatic amine compound of the present invention. In a case of afluorescent material which emits light with a longer wavelength, the useof the aromatic amine compound of the present invention can offer asimilar advantageous effect.

Specifically, the aromatic amine compound of the present invention iseffectively used for a layer which is in contact with a layer containinga phosphorescent material which emits phosphorescent light with arelatively short wavelength because of the following reason. Since thetriplet level of the aromatic amine compound of the present invention ishigh, the energy transfer from an excited phosphorescent material to thearomatic amine compound of the present invention does not easily occur.Therefore, the excited energy of the phosphorescent material can beextracted effectively as light emission. In addition, when the aromaticamine compound of the present invention is excited, the energy transferfrom the triplet level of the excited aromatic amine compound to thetriplet level of the phosphorescent material becomes possible and theluminous efficiency of the light-emitting element can be improved. Inthe case of using the aromatic amine compound of the present inventionfor a layer which is in contact with a layer containing a phosphorescentmaterial, it is more effective to provide a light-emitting region closeto a layer containing the aromatic amine compound of the presentinvention. In a case of a phosphorescent material which emits light witha longer wavelength, the use of the aromatic amine compound of thepresent invention can offer a similar advantageous effect.

In particular, the aromatic amine compound of the present invention ispreferably the aromatic amine compound expressed by General Formula (1),which has an asymmetrical structure, because the band gap is wider andmoreover the triplet level is high.

In addition, since the light-emitting element of the present inventionhas high luminous efficiency, the power consumption can be reduced.

Further, the aromatic amine compound of the present invention issuperior in a hole-transporting property. Therefore, the aromatic aminecompound of the present invention can be used for the hole-transportinglayer of the light-emitting element, which can provide a light-emittingelement with favorable characteristics.

Moreover, the aromatic amine compound expressed by General Formula (2)is superior in heat resistance. Therefore, the use of the aromatic aminecompound expressed by General Formula (2) can provide a device superiorin heat resistance.

Embodiment Mode 3

Embodiment Mode 3 will explain a light-emitting element with a structuredifferent from the structure shown in Embodiment Mode 2.

Since the aromatic amine compound of the present invention has a wideband gap and high triplet and singlet levels, the aromatic aminecompound of the present invention can be used for a host for dispersinga material with a light-emitting property. That is to say, the aromaticamine compound of the present invention can be used for the third layer105 shown in Embodiment Mode 2. As the material with a light-emittingproperty which is dispersed in the aromatic amine compound of thepresent invention, various fluorescent materials and phosphorescentmaterials can be used.

When the aromatic amine compound of the present invention is used forthe third layer 105, the second layer 104 can be formed of variousmaterials. For example, various aromatic amine compounds can be used. Asthe widely used materials, the following starburst aromatic aminecompounds are given: 4,4′-bis[N-(3-methylphenyl)-N-phenylamino]biphenyl;its derivative, 4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl(hereinafter referred to as NPB);4,4′,4″-tris(N,N-diphenyl-amino)triphenylamine;4,4′,4″-tris[N-(3-methylphenyl)-N-phenylamino]triphenylamine; and thelike. These are the substances mainly with a hole mobility of 10⁻⁶cm²/Vs or higher. However, other materials than these may also be usedas long as the hole-transporting property is higher than theelectron-transporting property. The second layer 104 may be not only asingle layer, but also a mixed layer or a stack of two or more layersincluding any of the aforementioned substances.

Since the aromatic amine compound of the present invention has a wideband gap, the aromatic amine compound of the present invention can beused for a host material of a light-emitting material which emits lightwith a short wavelength.

The aromatic amine compound of the present invention is effectively usedas a host material for a fluorescent material which emits fluorescentlight with a short wavelength, such as blue light, because of thefollowing reason. Since the aromatic amine compound of the presentinvention has high triplet level and singlet level, the energy transferfrom an excited fluorescent material to the aromatic amine compound ofthe present invention does not easily occur. Therefore, the excitedenergy of the fluorescent material can be extracted efficiently as lightemission. In addition, when the aromatic amine compound of the presentinvention is excited, the energy transfer from the triplet level or thesinglet level of the excited aromatic amine compound to thephosphorescent material becomes possible and the luminous efficiency ofthe light-emitting element can be improved. In a case of a fluorescentmaterial which emits light with a longer wavelength, the use of thearomatic amine compound of the present invention can offer a similaradvantageous effect.

The aromatic amine compound of the present invention is effectively usedas a host material for a phosphorescent material which emitsphosphorescent light with a relatively short wavelength, such as greenlight, because of the following reason. Since the triplet level of thearomatic amine compound of the present invention is high, the energytransfer from an excited phosphorescent material to the aromatic aminecompound of the present invention does not easily occur. Therefore, theexcited energy of the phosphorescent material can be extractedefficiently as light emission. In addition, when the aromatic aminecompound of the present invention is excited, the energy transfer fromthe triplet level of the excited aromatic amine compound to the tripletlevel of the phosphorescent material becomes possible and the luminousefficiency of the light-emitting element can be improved. In a case of aphosphorescent material which emits light with a longer wavelength, theuse of the aromatic amine compound of the present invention can offer asimilar advantageous effect.

In particular, the aromatic amine compound of the present invention ispreferably the aromatic amine compound expressed by General Formula (1)which has an asymmetrical structure, because the band gap is wider andmoreover the triplet level is also high.

Since the light-emitting element of the present invention has highluminous efficiency, the power consumption can be reduced.

In addition, the aromatic amine compound expressed by General Formula(2) is superior in heat resistance. Therefore, the use of the aromaticamine compound expressed by General Formula (2) can provide a devicesuperior in heat resistance.

Embodiment Mode 4

Embodiment Mode 4 will explain a light-emitting element having astructure different from those shown in Embodiment Modes 2 and 3.

When the aromatic amine compound of the present invention is used forthe third layer 105 shown in Embodiment Mode 2, light can be emittedfrom the aromatic amine compound of the present invention. Since thearomatic amine compound of the present invention emits violet to bluelight, a light-emitting element emitting violet to blue light can beobtained.

The third layer 105 may include only the aromatic amine compound of thepresent invention or may include the aromatic amine compound of thepresent invention which is dispersed in another substance. As thesubstance in which the aromatic amine compound of the present inventionis dispersed, various materials such as the following can be used inaddition to the substance with a high hole-transporting property and thesubstance with a high electron-transporting property described inEmbodiment Mode 2:3-(4-biphenylyl)-4-phenyl-5-(4-tert-butylphenyl)-1,2,4-triazole (abbr.:TAZ), 4,4′-di(N-carbazolyl)biphenyl (abbr.: CBP),2,2′,2″-(1,3,5-benzenetri-yl)-tris[1-phenyl-1H-benzimidazole] (abbr.:TPBI), and the like.

Since the aromatic amine compound of the present invention has a highglass transition point, a light-emitting element with the use of thearomatic amine compound of the present invention can have excellent heatresistance.

The aromatic amine compound of the present invention is stable evenafter repetition of oxidation reactions and subsequent reductionreactions. That is to say, the aromatic amine compound of the presentinvention is stable against repeated oxidation reactions. Therefore, alight-emitting element with the use of the aromatic amine compound ofthe present invention can have a long lifetime.

The structure shown in Embodiment Mode 2 or 3 can be appropriately usedexcept the third layer 105.

Embodiment Mode 5

Embodiment Mode 5 will explain a light-emitting element having astructure different from those described in Embodiment Modes 2 to 4.

Since the aromatic amine compound of the present invention has ahole-injecting property, the aromatic amine compound of the presentinvention can be used for the first layer 103 shown in Embodiment Mode2. Moreover, a composite material including the aromatic amine compoundof the present invention and an inorganic compound can be used for thefirst layer 103. The inorganic compound used for the composite materialis preferably an oxide of a transition metal. In addition, an oxide of ametal belonging to any of Groups 4 to 8 in the periodic table can begiven. Specifically, vanadium oxide, niobium oxide, tantalum oxide,chromium oxide, molybdenum oxide, tungsten oxide, manganese oxide, andrhenium oxide are preferable because of their high electron-acceptingproperty. Above all, molybdenum oxide is preferable because it is stablein the air, easily handled, and has a low moisture-absorption property.

In the composite material including the aromatic amine compound of thepresent invention and the inorganic compound, electrons are transportedbetween the organic compound and the inorganic compound to increasecarrier density; therefore, the hole-injecting property and thehole-transporting property are excellent. When the first layer 103 isformed of the composite material including the aromatic amine compoundof the present invention and the inorganic compound, ohmic contact withthe first electrode 102 is possible; thus, the material for forming thefirst electrode can be selected regardless of the work function.

When the aromatic amine compound of the present invention is used forthe first layer 103, the second layer 104 can be formed of variousmaterials. For example, an aromatic amine compound (i.e., having a bondof a benzene ring and nitrogen) can be used. As the widely usedmaterial, the following starburst aromatic amine compounds are given:4,4′-bis[N-(3-methylphenyl)-N-phenylamino]biphenyl; its derivative,4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (hereinafter referred toas NPB); 4,4′,4″-tris(N,N-diphenyl-amino)triphenylamine;4,4′,4″-tris[N-(3-methylphenyl)-N-phenylamino]triphenylamine; and thelike. These are the substances mainly with a hole mobility of 10⁻⁶cm²/Vs or higher. However, other materials than these may also be usedas long as the hole-transporting property is higher than theelectron-transporting property. The second layer 104 may be not only asingle layer, but also a mixed layer or a stack of two or more layersincluding any of the aforementioned substances.

The aromatic amine compound of the present invention may be used for thefirst layer 103 and the second layer 104.

Since the aromatic amine compound of the present invention has ahole-injecting property, the aromatic amine compound of the presentinvention can be used as the hole-injecting layer of the light-emittingelement.

In addition, since the aromatic amine compound of the present inventionhas a high glass transition point, the light-emitting element with theuse of the aromatic amine compound of the present invention can haveexcellent heat resistance.

The aromatic amine compound of the present invention is stable evenafter repetition of an oxidation reaction and a subsequent reductionreaction. That is to say, the aromatic amine compound of the presentinvention is stable against repeated oxidation reactions. Therefore, alight-emitting element with the use of the aromatic amine compound ofthe present invention can have a long lifetime.

The structure shown in any of Embodiment Modes 2 to 4 can beappropriately used except the first layer 103.

Embodiment Mode 6

In this embodiment mode, a mode of a light-emitting element in which aplurality of light-emitting units of the present invention are stacked(hereinafter this light-emitting element is referred to as astacked-type element) will be described with reference to FIG. 9. Thelight-emitting element includes a plurality of light-emitting unitsbetween a first electrode and a second electrode. Each of thelight-emitting units may have a similar structure to that of the layercontaining a light-emitting substance shown in Embodiment Mode 2. Thatis, the light-emitting element shown in Embodiment Mode 2 is alight-emitting element having one light-emitting unit, whereas thelight-emitting element described in this embodiment mode has a pluralityof light-emitting units.

In FIG. 9, a first light-emitting unit 511 and a second light-emittingunit 512 are stacked between a first electrode 501 and a secondelectrode 502. The first electrode 501 and the second electrode 502 maybe similar to the electrodes shown in Embodiment Mode 2. The firstlight-emitting unit 511 and the second light-emitting unit 512 may haveeither the same structure or a different structure, which may be similarto those described in Embodiment Modes 2 to 5.

A charge-generating layer 513 includes a composite material of anorganic compound and a metal oxide. The composite material of an organiccompound and a metal oxide includes the organic compound shown inEmbodiment Mode 2 and a metal oxide such as vanadium oxide, molybdenumoxide, or tungsten oxide. As the organic compound, various compoundssuch as an aromatic amine compound, a carbazole derivative, aromatichydrocarbon, and a high molecular compound (oligomer, dendrimer,polymer, or the like) can be used. As the organic compound, it ispreferable to use the organic compound which has a hole-transportingproperty and has a hole mobility of 10⁻⁶ cm²/Vs or higher. However,other substances than these may also be used as long as thehole-transporting property is higher than the electron-transportingproperty. The composite material of the organic compound and the metaloxide can achieve low-voltage driving and low-current driving because ofsuperior carrier-injecting property and carrier-transporting property.

Alternatively, the charge-generating layer 513 may be formed bycombining the composite material of the organic compound and the metaloxide with another material. For example, a layer containing thecomposite material of the organic compound and the metal oxide may becombined with a layer containing a compound of a substance selected fromsubstances with an electron-donating property and a compound with a highelectron-transporting property. Moreover, a layer containing thecomposite material of the organic compound and the metal oxide may becombined with a transparent conductive film.

In any case, it is acceptable as long as the charge-generating layer 513interposed between the first light-emitting unit 511 and the secondlight-emitting unit 512 injects electrons to one of these light-emittingunits and holes to the other when voltage is applied to the firstelectrode 501 and the second electrode 502.

Although this embodiment mode describes the light-emitting elementhaving two light-emitting units, the present invention can be similarlyapplied to a light-emitting element in which three or morelight-emitting units are stacked. When the charge-generating layer isprovided between the pair of electrodes so as to partition the plurallight-emitting units like the light-emitting element of this embodimentmode, the element can have long lifetime in a high luminous region whilekeeping low current density. When the light-emitting element is appliedfor illumination, voltage drop due to resistance of an electrodematerial can be reduced, thereby achieving homogeneous light emission ina large area. Moreover, a light-emitting device of low powerconsumption, which can be driven at low voltage, can be achieved.

This embodiment mode can be appropriately combined with anotherembodiment mode.

Embodiment Mode 7

Embodiment Mode 7 will explain a light-emitting device manufactured byusing an aromatic amine compound of the present invention.

In this embodiment mode, a light-emitting device manufactured by usingan aromatic amine compound of the present invention is explained withreference to FIGS. 3A and 3B. FIG. 3A is a top view of thelight-emitting device, while FIG. 3B is a cross-sectional view along aline A-A′ and a line B-B′. This light-emitting device includes a drivercircuit portion (source side driver circuit) 601, a pixel portion 602,and a driver circuit portion (gate side driver circuit) 603 which areshown by dashed lines in order to control the light emission of thelight-emitting element. Moreover, reference numeral 604 denotes asealing substrate; 605, a sealant; and 607, a space surrounded by thesealant 605.

A lead wiring 608 is to transmit signals to be inputted to the sourceside driver circuit 601 and the gate side driver circuit 603 and receivea video signal, a clock signal, a start signal, a reset signal, and thelike from an FPC (Flexible Printed Circuit) 609 which is an externalinput terminal. Although only an FPC is shown here, this FPC may have aprinted wiring board (PWB) attached. In this specification, thelight-emitting device includes not only a light-emitting device alonebut also a light-emitting device with an FPC or a PWB attached thereto.

Next, the cross-sectional structure is explained with reference to FIG.3B. Although the driver circuit portion and the pixel portion are formedover an element substrate 610, the source side driver circuit 601 as thedriver circuit portion and one pixel in the pixel portion 602 are shownhere.

In the source side driver circuit 601, a CMOS circuit in which ann-channel TFT 623 and a p-channel TFT 624 are combined is formed. Thedriver circuit may be formed by various CMOS circuits, PMOS circuits, orNMOS circuits. Although this embodiment mode shows a driver-integratedtype in which the driver circuit is formed over the substrate, thestructure may be different. For example, the driver circuit may beformed not over the substrate but outside the substrate.

Moreover, the pixel portion 602 is formed by a plurality of pixelsincluding a switching TFT 611, a current controlling TFT 612, and afirst electrode 613 electrically connected to a drain of the currentcontrolling TFT 612. An insulator 614 is formed covering an end portionof the first electrode 613. Here, the insulator 614 is formed using apositive photosensitive acrylic resin film.

In order to have favorable coverage, the insulator 614 is formed so asto have a curved surface with curvature at its upper end or lower endportion. For example, in a case of using a positive photosensitiveacrylic for the insulator 614, only the upper end portion of theinsulator 614 preferably has a curved surface with a radius of curvatureof 0.2 to 3 μm. As the insulator 614, either a negative type whichbecomes insoluble in etchant by light irradiation or a positive typewhich becomes soluble in etchant by light irradiation can be used.

A layer 616 containing a light-emitting substance and a second electrode617 are formed over the first electrode 613. Here, the first electrode613 functioning as an anode is preferably formed of a material with ahigh work function. For example, a single-layer film of an ITO film, anindium tin oxide film including silicon, an indium oxide film containing2 to 20 wt % of zinc oxide, a titanium nitride film, a chromium film, atungsten film, a Zn film, a Pt film, or the like can be used. Besidesthese single-layer films, a stack of a film containing titanium nitrideas its main component and a film containing aluminum as its maincomponent, a stack of three layers of a titanium nitride film, a filmcontaining aluminum as its main component, and a titanium nitride film,or the like can be used. When a stacked-layer structure is employed, thefirst conductive film 613 can have low resistance as wiring, obtainfavorable ohmic contact, and moreover function as an anode.

The layer 616 containing a light-emitting substance is formed by variousmethods such as an evaporation method using an evaporation mask, aninkjet method, or a spin coating method. The layer 616 containing alight-emitting substance includes the aromatic amine compound of thepresent invention shown in Embodiment Mode 1. As another material forforming the layer 616 containing a light-emitting substance, a lowmolecular material or a high molecular material (including oligomer anddendrimer) may be used.

The second electrode 617 which is formed over the layer 616 containing alight-emitting substance and functions as a cathode is preferably formedof a material with a low work function (Al, Mg, Li, Ca, or an alloy orcompound thereof such as MgAg, MgIn, AlLi, LiF, or CaF₂). When lightgenerated in the layer 616 containing a light-emitting substance passesthrough the second electrode 617, the second electrode 617 is preferablyformed by a stack of a thin metal film and a transparent conductive film(ITO, indium oxide including 2 to 20 wt % of zinc oxide, indium tinoxide including silicon, zinc oxide (ZnO), or the like).

When the sealing substrate 604 and the element substrate 610 areattached to each other with the sealant 605, the light-emitting element618 is provided in the space 607 surrounded by the element substrate610, the sealing substrate 604, and the sealant 605. The space 607 isfilled with a filler, which may be an inert gas (such as nitrogen orargon) or the sealant 605.

The sealant 605 is preferably formed of an epoxy-based resin. It isdesirable that the material of the sealant 605 preferably allows aslittle moisture and oxygen as possible to penetrate. As the sealingsubstrate 604, a plastic substrate formed of FRP (Fiberglass-ReinforcedPlastics), PVF (polyvinyl fluoride), polyester, acrylic, or the like canbe used besides a glass substrate or a quartz substrate.

As described above, the light-emitting device manufactured by thearomatic amine compound of the present invention can be obtained.

The light-emitting device of the present invention uses the aromaticamine compound shown in Embodiment Mode 1; therefore, the light-emittingdevice can have favorable characteristics. In specific, thelight-emitting device can have high luminous efficiency.

The aromatic amine compound expressed by General Formula (2) is superiorin heat resistance. Therefore, the light-emitting device using thearomatic amine compound expressed by General Formula (2) can haveexcellent heat resistance.

This embodiment mode thus describes the active light-emitting device inwhich the driving of the light-emitting element is controlled by atransistor. However, the light-emitting device may be of passive type inwhich the light-emitting element is driven without particularlyproviding an element for driving, such as a transistor. FIG. 4 is aperspective view of a passive light-emitting device manufactured byapplying the present invention. In FIG. 4, a layer 955 containing alight-emitting substance is provided over a substrate 951 and between anelectrode 952 and an electrode 956. End portions of the electrode 952are covered with an insulating layer 953. Then, a partition wall layer954 is provided over the insulating layer 953. A side wall of thepartition wall layer 954 slopes so that a distance between one side walland the other side wall becomes narrow toward a substrate surface. Inother words, a cross section of the partition wall layer 954 in thedirection of a narrow side is trapezoidal, and a base (a side facing ina similar direction to a plane direction of the insulating layer 953 andbeing in contact with the insulating layer 953) is shorter than an upperside (a side facing in a similar direction to the plane direction of theinsulating layer 953 and not being in contact with the insulating layer953). A defect of the light-emitting element due to static electricityor the like can be prevented by providing the partition wall layer 954in this manner. In addition, the passive-type light-emitting device canalso have high luminous efficiency and excellent heat resistance when itincludes the light-emitting element of the present invention with highluminous efficiency. Moreover, the high luminous efficiency leads to lowpower consumption.

Embodiment Mode 8

This embodiment mode explains an electronic appliance of the presentinvention which includes the light-emitting device described inEmbodiment Mode 7 as its component. The electronic appliance of thepresent invention includes the aromatic amine compound of the presentinvention described in Embodiment Mode 1 and has a display portion withhigh heat resistance and high luminous efficiency. The high luminousefficiency leads to low power consumption.

Examples of the electronic appliance having the light-emitting elementmanufactured using the aromatic amine compound of the present inventioninclude the following: a camera such as a video camera or a digitalcamera, a goggle type display, a navigation system, a sound reproducingdevice (a car audio system, an audio component, or the like), acomputer, a game machine, a mobile information terminal (a mobilecomputer, a cellular phone, a mobile game machine, an electronic book,or the like), an image reproducing device having a recording medium(specifically, a device which reproduces a recording medium such as adigital versatile disc (DVD) and has a display device for displaying theimage), and the like. Specific examples of these electronic appliancesare shown in FIGS. 5A to 5D.

FIG. 5A shows a television device according to the present invention,which includes a housing 9101, a support base 9102, a display portion9103, speaker portions 9104, a video input terminal 9105, and the like.In this television device, the display portion 9103 includeslight-emitting elements similar to those described in Embodiment Modes 2to 6, which are arranged in matrix. The light-emitting element hasfeatures of high luminous efficiency and high heat resistance. Thedisplay portion 9103 which includes the light-emitting element also hasa similar feature. Therefore, in this television device, image qualitydoes not deteriorate much and power consumption is reduced. With suchfeatures, a deterioration compensation circuit and a power supplycircuit can be significantly reduced or downsized in the televisiondevice, thereby achieving reduction in size and weight of the housing9101 and the support base 9102. Since reduction in power consumption,improvement in image quality, and reduction in size and weight areachieved in the television device according to the present invention, aproduct which is suitable for a living environment can be provided.

FIG. 5B shows a computer according to the present invention, whichincludes a main body 9201, a housing 9202, a display portion 9203, akeyboard 9204, an external connection port 9205, a pointing mouse 9206,and the like. In this computer, the display portion 9203 includeslight-emitting elements similar to those described in Embodiment Modes 2to 6, which are arranged in matrix. The light-emitting element hasfeatures of high luminous efficiency and high heat resistance. Thedisplay portion 9203 which includes the light-emitting element has asimilar feature. Therefore, in this computer, image quality does notdeteriorate much and power consumption is reduced. With such features, adeterioration compensation circuit and a power supply circuit can besignificantly reduced or downsized in the computer, thereby achievingreduction in size and weight of the main body 9201 and the housing 9202.Since reduction in power consumption, improvement in image quality, andreduction in size and weight thereof are achieved in the computeraccording to the present invention, a product which is suitable forenvironment can be provided.

FIG. 5C shows a cellular phone according to the present invention, whichincludes a main body 9401, a housing 9402, a display portion 9403, anaudio input portion 9404, an audio output portion 9405, operation keys9406, an external connection port 9407, an antenna 9408, and the like.In this cellular phone, the display portion 9403 includes light-emittingelements similar to those described in Embodiment Modes 2 to 6, whichare arranged in matrix. The light-emitting element has features of highluminous efficiency and high heat resistance. The display portion 9403which includes the light-emitting element also has a similar feature.Therefore, in this cellular phone, image quality does not deterioratemuch and power consumption is reduced. With such features, adeterioration compensation circuit and a power supply circuit can besignificantly reduced or downsized in the cellular phone, therebyachieving reduction in size and weight of the main body 9401 and thehousing 9402. Since reduction in power consumption, improvement in imagequality, and reduction in size and weight thereof are achieved in thecellular phone according to the present invention, a product which issuitable for being carried can be provided.

FIG. 5D shows a camera according to the present invention, whichincludes a main body 9501, a display portion 9502, a housing 9503, anexternal connection port 9504, a remote control receiving portion 9505,an image receiving portion 9506, a battery 9507, an audio input portion9508, an operation key 9509, an eye piece portion 9510, and the like. Inthis camera, the display portion 9502 includes light-emitting elementssimilar to those described in Embodiment Modes 2 to 6, which arearranged in matrix. The light-emitting element has features of highluminous efficiency and high heat resistance. The display portion 9502which includes the light-emitting element also has similar features.Therefore, in this camera, image quality does not deteriorate much andpower consumption is reduced. With such features, a deteriorationcompensation circuit and a power supply circuit can be significantlyreduced or downsized in the camera, thereby achieving reduction in sizeand weight of the main body 9501. Since reduction in power consumption,improvement in image quality, and reduction in size and weight thereofare achieved in the camera according to the present invention, a productwhich is suitable for being carried can be provided.

As described above, the applicable range of the light-emitting device ofthe present invention is so wide that the light-emitting device can beapplied to electronic appliances of various fields. By the use of thearomatic amine compound of the present invention, an electronicappliance including a display portion with high luminous efficiency andhigh heat resistance can be provided.

In addition, the light-emitting device of the present invention can alsobe used as an illumination apparatus. One mode of using thelight-emitting element of the present invention as an illuminationapparatus is explained with reference to FIG. 6.

FIG. 6 shows an example of a liquid crystal display device using thelight-emitting device of the present invention as a backlight. Theliquid crystal display device shown in FIG. 6 includes a housing 901, aliquid crystal layer 902, a backlight 903, and a housing 904. The liquidcrystal layer 902 is connected to a driver IC 905. The light-emittingdevice of the present invention is used as the backlight 903, to whichcurrent is supplied through a terminal 906.

By the use of the light-emitting device of the present invention as abacklight of the liquid crystal display device, the backlight can havehigh luminous efficiency. Since the light-emitting device of the presentinvention is a surface light-emitting illumination apparatus and can beformed to have a large area, a larger-area backlight can be obtained anda larger-area liquid crystal display device can also be obtained.Further, the light-emitting device of the present invention is thin andconsumes less electric power; therefore, reduction in thickness andpower consumption of the display device can also be achieved. Moreover,since the light-emitting device of the present invention is superior inheat resistance, the liquid crystal display device using thelight-emitting device of the present invention is also superior in heatresistance.

FIG. 7 shows an example in which the light-emitting device of thepresent invention is used as a desk lamp, which is an illuminationapparatus. The desk lamp shown in FIG. 7 includes a housing 2001 and alight source 2002. The light-emitting device of the present invention isused as the light source 2002. Since the light-emitting device of thepresent invention is capable of emitting light with high luminance, anelaborate operation and the like can be efficient by having the deviceat hand.

FIG. 8 shows an example of using the light-emitting device of thepresent invention as an illumination apparatus 3001 in the room. Sincethe light-emitting device of the present invention can be enlarged, thelight-emitting device can be used as a large-area illuminationapparatus. Moreover, since the light-emitting device of the presentinvention is thin and consumes less electric power, the light-emittingdevice can be used as the thin illumination apparatus consuming lesselectric power. Thus, a television device 3002 of the present inventionsimilar to the television device described with reference to FIG. 5A canbe installed in the room using the light-emitting device of the presentinvention as the illumination apparatus 3001, so that pubic broadcastingand movies can be enjoyed. In such a case, since both of the televisiondevice and the illumination apparatus consume less electric power, it ispossible to enjoy dynamic images in the bright room without worryingabout electricity charges.

Embodiment 1

Embodiment 1 will explain a method of synthesizingN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine(abbr: YGAF) expressed by Structure Formula (21).

[Step 1]

A method of synthesizing 9-[4-(N-phenylamino)phenyl]carbazole (abbr.:YGA) is explained.

(i) Synthesis of N-(4-bromophenyl)carbazole

Synthesis Scheme (C-1) of N-(4-bromophenyl)carbazole is hereinaftershown.

First, a method of synthesizing N-(4-bromophenyl)carbazole is explained.In a three-necked flask of 300 mL content, 56.3 g (0.24 mol) of1,4-dibromobenzene, 31.3 g (0.18 mol) of carbazole, 4.6 g (0.024 mol) ofcopper iodide, 66.3 g (0.48 mol) of potassium carbonate, and 2.1 g(0.008 mol) of 18-crown-6-ether were mixed and nitrogen substitution wascarried out. Then, 8 mL of1,3-dimethyl-3,4,5,6-tetrahydro-2(1H)-pyrimidinone (abbr.: DMPU) wasadded and stirred for six hours at 180° C. After the reaction mixturewas cooled down to room temperature, the sediment was removed by suctionfiltration. The filtrate was washed with diluted hydrochloric acid, asaturated sodium hydrogen carbonate aqueous solution, and saturatedsaline in this order and then dried with magnesium sulfate. After thedrying, the reaction mixture was naturally filtered and concentrated,and then the obtained oil-like substance was purified by silica gelcolumn chromatography (hexane: ethyl acetate=9:1) and recrystallized bychloroform and hexane. Then, the target matter, i.e., a light-brownplate-like crystal of N-(4-bromophenyl)carbazole was obtained for 20.7 gwith a yield of 35%. It was confirmed that this compound wasN-(4-bromophenyl)carbazole by nuclear magnetic resonance spectroscopy(NMR).

The ¹H-NMR data on this compound is shown. A ¹H-NMR (300 MHz, CDCl₃):δ=8.14 (d, J=7.8 Hz, 2H), δ=7.73 (d, J=8.7 Hz, 2H), δ=7.46 (d, J=8.4 Hz,2H), and δ=7.42-7.26 (m, 6H).

(ii) Synthesis of 9-[4-(N-phenylamino)phenyl]carbazole (abbr.: YGA)

Synthesis Scheme (C-2) of YGA is hereinafter shown.

In a three-necked flask of 200 mL content, 5.4 g (17.0 mmol) ofN-(4-bromophenyl)carbazole obtained by the aforementioned step (i), 1.8mL (20.0 mmol) of aniline, 100 mg (0.17 mmol) ofbis(dibenzylideneacetone)palladium(0), and 3.9 g (40 mmol) of sodiumtert-butoxide were mixed and nitrogen substitution was carried out.Then, 0.1 mL of tri(tert-butyl)phosphine (10 wt % hexane solution) and50 mL of toluene were added and stirred for six hours at 80° C. Afterthe reaction mixture was filtered through Florisil, celite, and alumina,the filtrate was washed with water or saturated saline and then driedwith magnesium sulfate. The reaction mixture was naturally filtered andconcentrated, and then the obtained oil-like substance was purified bysilica gel column chromatography (hexane: ethyl acetate=9:1), whereby9-[4-(N-phenylamino)phenyl]carbazole (abbr.: YGA) as the target matteris obtained for 4.1 g with a yield of 73%. By the use of nuclearmagnetic resonance spectroscopy (NMR), it was confirmed that thiscompound was 9-[4-(N-phenylamino)phenyl]carbazole (abbr.: YGA).

The ¹H-NMR data on the compound is shown. A ¹H-NMR (300 MHz, DMSO-d₆):δ=8.47 (s, 1H), δ=8.22 (d, J=7.8 Hz, 2H), δ=7.44-7.16 (m, 14H), andδ=6.92-6.87 (m, 1H). In addition, a ¹H-NMR chart is also shown in FIGS.10A and 10B. FIG. 10B is a chart showing an enlarged part in the rangeof 6.7 ppm to 8.6 ppm of FIG. 10A.

[Step 2]

A method of synthesizingN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine(abbr.: YGAF) expressed by Structure Formula (21) is explained.Synthesis Scheme (D-1) is shown below.

In a three-necked flask of 300 mL content, 2.9 g (10 mmol) of2-bromo-9,9-dimethylfluorene, 3.34 g (10 mmol) of4-(carbazol-9-yl)diphenylamine, 115 mg (0.2 mmol) ofbis(dibenzylideneacetone)palladium(0), and 3.0 g (31.2 mmol) oftert-butoxysodium were mixed and nitrogen substitution was carried out.Then, 100 mL of toluene and 0.2 mL of tri(tert-butyl)phosphine (10 wt %hexane solution) were added and stirred for five hours at 80° C. Afterthe reaction, the reaction solution was filtered through celite,Florisil, and alumina, the filtrate was washed with water, and a waterlayer was abstracted with toluene. The abstracted solution was washedwith saturated saline together with an organic layer and then dried withmagnesium sulfate. After the obtained reaction mixture was naturallyfiltered, the filtrate was concentrated to obtain a solid. When thesolid was purified with silica gel column chromatography (hexane:toluene=7:3), 3.6 g of a white solid, which is a target matter, wasobtained with a yield of 64%. It was confirmed by nuclear magneticresonance spectroscopy (NMR) that this compound wasN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine(abbr.: YGAF) expressed by Structure Formula (21).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz,DMSO-d₆): δ=1.40 (s, 6H), 7.09-7.53 (m, 20H), 7.75-7.77 (m, 1H), 7.81(d, J=8.4 Hz, 1H), and 8.23 (d, J=7.5 Hz, 2H). A ¹H-NMR chart is alsoshown in FIGS. 11A and 11B. Further, FIG. 11B is a chart showing anenlarged part in the range of 6.0 ppm to 9.0 ppm of FIG. 11A.

The obtained YGAF with an amount of 635 mg was then purified bysublimation for 12 hours at 230° C. under 200 Pa in the flow of argongas at a rate of 20.0 mL/min; thus, 485 mg of a light yellow solid ofYGAF was obtained with a yield of 76%.

Further, when a decomposition temperature (T_(d)) of the thus obtainedYGAF was measured by a thermo-gravimetric/differential thermal analyzer(TG/DTA 320, manufactured by Seiko Instruments Inc.), the T_(d) was 313°C.

In addition, the glass transition point was measured by a differentialscanning calorimeter (DSC, manufactured by PerkinElmer, Inc., Pyris 1).First, a sample was heated up to 300° C. at 40° C./min, and then it wascooled down to room temperature at 40° C./min. After that, thetemperature was raised to 300° C. at 10° C./min and then lowered to roomtemperature at 10° C./min, thereby obtaining the DSC chart shown in FIG.12. In FIG. 12, the X axis shows temperature and the Y axis shows heatflow. The Y axis shows endotherm in an upward direction. It wasunderstood from this chart that the glass transition point (T_(g)) ofYGAF was 91° C.

FIG. 13 shows an absorption spectrum of a toluene solution of YGAF. FIG.14 shows an absorption spectrum of a thin film of YGAF. The measurementwas conducted by using a UV-visible spectrophotometer (V-550,manufactured by Japan Spectroscopy Corporation). The solution was put ina quartz cell, and the thin film was evaporated on a quartz substrate toform the samples. Their absorption spectra from each of which theabsorption spectrum of quartz is subtracted are shown in FIGS. 13 and14. In FIGS. 13 and 14, the horizontal axis shows a wavelength (nm)while the vertical axis shows absorption intensity (arbitrary unit). Inthe case of the toluene solution, absorption was observed at around 326to 362 nm, and in the case of the thin film, it was observed at around343 nm. The light emission spectrum of the toluene solution of YGAF(excitation wavelength: 340 nm) is shown in FIG. 15, while that of thethin film of YGAF (excitation wavelength: 343 nm) is shown in FIG. 16.In FIGS. 15 and 16, the horizontal axis shows a wavelength (nm) and thevertical axis shows light emission intensity (arbitrary unit). Themaximum light emission wavelength was 384 nm in the case of the toluenesolution (excitation wavelength: 340 nm), and 396 nm in the case of thethin film (excitation wavelength: 343 nm).

In addition, the HOMO level of YGAF in the thin film state was −5.39 eV,which was measured by photoelectron spectrometer (AC-2, manufactured byRiken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of YGAF in FIG. 14. When the absorption edge was estimated asan optical energy gap, the energy gap was 3.25 eV. Therefore, the LUMOlevel was −2.14 eV.

Moreover, the oxidation reaction characteristic of YGAF was measured bycyclic voltammetry (CV) measurement. Further, an electrochemicalanalyzer (ALS model 600A, manufactured by BAS Inc.) was used for themeasurement.

As for a solution used in the CV measurement, dehydrateddimethylformamide (DMF, manufactured by Aldrich, 99.8%, catalog number:22705-6) was used as a solvent. Tetra-n-butylammonium perchlorate(n-Bu₄NClO₄, manufactured by Tokyo Chemical Industry Co., Ltd., catalognumber: T0836), which was a supporting electrolyte, was dissolved in thesolvent such that the concentration of the tetra-n-butylammoniumperchlorate was 100 mmol/L. Moreover, the object to be measured wasdissolved such that the concentration thereof was set to be 1 mmol/L.Further, a platinum electrode (a PTE platinum electrode, manufactured byBAS Inc.) was used as a work electrode. A platinum electrode (a VC-3 Ptcounter electrode (5 cm), manufactured by BAS Inc.) was used as anauxiliary electrode. An Ag/Ag⁺ electrode (an RE5 nonaqueous solventreference electrode, manufactured by BAS Inc.) was used as a referenceelectrode. It is to be noted that the measurement was conducted at roomtemperature.

The oxidation reaction characteristic of YGAF was measured as follows. Ascan for changing the potential of the work electrode with respect tothe reference electrode from 0.8 V to −0.12 V after changing thepotential from −0.12 V to 0.8 V was set as one cycle, and 100 cycleswere measured. Further, the scanning speed of the CV measurement was setto be 0.1 V/s.

A result of the measurement on the oxidation reaction characteristic ofYGAF is shown in FIG. 17, in which the horizontal axis shows thepotential (V) of the work electrode with respect to the referenceelectrode, while the vertical axis shows a value (μA) of current flowingbetween the work electrode and the auxiliary electrode.

In FIG. 17, a current indicating oxidation was observed at around 0.62 V(vs. Ag/Ag⁺ electrode). Regardless of the repetition of 100-cycle scans,the peak position and the peak intensity at the CV curve hardly changesin the oxidation reaction. Based on this fact, it was understood thatthe aromatic amine compound of the present invention is quite stableagainst the oxidation reaction and the subsequent reduction reaction(that is, repetition of oxidation).

An optimal molecular structure of YGAF in a ground state was calculatedwith B3LYP/6-311 (d, p) of density functional theory (DFT). The accuracyof calculation of the DFT is higher than that of Hartree-Fock (HF) whichdoes not consider electron correlation. In addition, the calculationcost of the DFT is lower than that of a method of perturbation (MP)which has the same level accuracy of calculation as the DFT. Therefore,the DFT was employed in the present calculation. The calculation wasperformed using a high-performance computer (HPC) (manufactured by SGIJapan, Ltd., Altix3700 DX).

In addition, the triplet-excitation energy (energy gap) of YGAF wascalculated by employing B3LYP/6-311 (d, p) of time-dependent densityfunctional theory (TDDFT) for the molecular structure whose structurewas optimized by the DFT. The triplet-excitation energy was calculatedto be 2.70 eV. Thus, it was understood from the calculation result thatthe aromatic amine compound of the present invention has hightriplet-excitation energy.

Embodiment 2

This embodiment will explain a method of synthesizing4-(carbazol-9-yl)phenyl-4′-phenyltriphenylamine (abbr.: YGA1BP)expressed by Structure Formula (52). Synthesis Scheme (D-2) is shownbelow.

In a three-necked flask of 300 mL content, 2.33 g (10 mmol) of4-bromobiphenyl, 3.30 g (10 mmol) of 4-(carbazol-9-yl)diphenylamine, 56mg (0.1 mmol) of bis(dibenzylideneacetone)palladium(0), and 3.0 g (31.2mmol) of tert-butoxysodium were put and nitrogen substitution wascarried out. Then, 20 mL of toluene and 0.1 mL oftri(tert-butyl)phosphine (10 wt % hexane solution) were added andstirred for five hours at 80° C. After the reaction, the reactionmixture was filtered through celite, Florisil, and alumina, the filtratewas washed with water, and a water layer was abstracted with toluene.The abstracted solution was washed with saturated saline together withan organic layer and then dried with magnesium sulfate. After theobtained reaction mixture was naturally filtered, the filtrate wasconcentrated to obtain a solid. When the solid was purified with silicagel column chromatography (hexane: toluene=7:3) and the obtained solidwas recrystallized by toluene and hexane, 4.2 g of a white powder-likesolid, which is a target matter, was obtained with a yield of 86%. Itwas confirmed by nuclear magnetic resonance spectroscopy (NMR) that thiscompound was 4-(9-carbazol-9-yl)phenyl-4′-phenyltriphenylamine (abbr.:YGA1BP) expressed by Structure Formula (52).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz,DMSO-d₆): δ=7.12-7.47 (m, 18H), 7.53 (d, J=8.7 Hz, 2H), 7.68-7.64 (m,4H), and 8.23 (d, J=7.8 Hz, 2H). A ¹H-NMR chart is also shown in FIGS.18A and 18B. Further, FIG. 18B is a chart showing an enlarged part inthe range of 6.0 ppm to 9.0 ppm of FIG. 18A.

The obtained YGA1BP with an amount of 694 mg was then purified bysublimation for five hours at 280° C. under 200 Pa in the flow of argongas at a rate of 20.0 mL/min; thus, 544 mg of an achromatous solid ofYGA1BP was obtained with a yield of 78%.

A thermogravimetry-differential thermal analysis (TG-DTA) of YGA1BP wasconducted by using a high vacuum differential type differential thermalbalance (manufactured by Bruker AXS K.K., DTA2410SA). When themeasurement was conducted under normal pressure with atemperature-rising speed of 10° C./min, the temperature at which theweight becomes 95% or lower of the weight at the start of themeasurement was 398° C. from the relation between the weight andtemperature (thermogravimetry).

FIG. 19 shows an absorption spectrum of a toluene solution of YGA1BP.The measurement was conducted by using a UV-visible spectrophotometer(V-550, manufactured by Japan Spectroscopy Corporation). The solutionwas put in a quartz cell. The absorption spectrum from which theabsorption spectrum of quartz is subtracted is shown in FIG. 19. In FIG.19, the horizontal axis shows a wavelength (nm) while the vertical axisshows absorption intensity (arbitrary unit). In the case of the toluenesolution, absorption was observed at around 324 nm. The light emissionspectrum of the toluene solution of YGA1BP (excitation wavelength: 340nm) is shown in FIG. 20. In FIG. 20, the horizontal axis shows awavelength (nm) and the vertical axis shows light emission intensity(arbitrary unit). The maximum light emission wavelength was 387 nm inthe case of the toluene solution (excitation wavelength: 340 nm).

An optimal molecular structure of YGA1BP in a ground state wascalculated with B3LYP/6-311 (d, p) of density functional theory (DFT).The accuracy of calculation of the DFT is higher than that ofHartree-Fock (HF) which does not consider electron correlation. Inaddition, the calculation cost of the DFT is lower than that of a methodof perturbation (MP) which has the same level accuracy of calculation asthe DFT. Therefore, the DFT was employed in the present calculation. Thecalculation was performed using a high-performance computer (HPC)(manufactured by SGI Japan, Ltd., Altix3700 DX).

In addition, the triplet-excitation energy (energy gap) of YGA1BP wascalculated by employing B3LYP/6-311 (d, p) of time-dependent densityfunctional theory (TDDFT) for the molecular structure whose structurewas optimized by the DFT. The triplet-excitation energy was calculatedto be 2.87 eV. Thus, it was understood from the calculation result thatthe aromatic amine compound of the present invention has hightriplet-excitation energy.

Embodiment 3

This embodiment will explain a method of synthesizingN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine(abbr.: YGA2F) expressed by Structure Formula (71). Synthesis Scheme(D-3) is shown below.

In a three-necked flask of 300 mL content, 1.7 g (3.8 mmol) of2,7-diiodo-9,9-dimethylfluorene, 2.5 g (7.6 mmol) of4-(carbazol-9-yl)diphenylamine, 44 mg (0.2 mmol) ofbis(dibenzylideneacetone)palladium(0), and 2.0 g (20 mmol) oftert-butoxysodium were put and nitrogen substitution was carried out.Then, 30 mL of toluene and 0.1 mL of tri(tert-butyl)phosphine (10 wt %hexane solution) were added and stirred for 12 hours at 80° C. After thereaction, the reaction mixture was filtered through celite, Florisil,and alumina, the filtrate was washed with water, and a water layer wasabstracted with toluene. The abstracted solution was washed withsaturated saline together with an organic layer and then dried withmagnesium sulfate. After the obtained reaction mixture was naturallyfiltered, the filtrate was concentrated to obtain a solid. When thesolid was purified with silica gel column chromatography (hexanetoluene=6:4) and the obtained compound was recrystallized by toluene andhexane, 2.9 g of a light yellow powder-like solid, which is a targetmatter, was obtained with a yield of 89%. It was confirmed by nuclearmagnetic resonance spectroscopy (NMR) that this compound wasN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine(abbr.: YGA2F) expressed by Structure Formula (71).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz,DMSO-d₆): δ=1.37 (s, 6H), 7.06-7.51 (m, 34H), 7.76 (d, J=8.4 Hz, 2H),and 8.22 (d, J=7.8 Hz, 4H). A ¹H-NMR chart is also shown in FIGS. 21Aand 21B. Further, FIG. 21B is a chart showing an enlarged part in therange of 6.0 ppm to 9.0 ppm of FIG. 21A.

The obtained YGA2F with an amount of 670 mg was then purified bysublimation for 15 hours at 420° C. under 200 Pa in the flow of argongas at a rate of 3.0 mL/min; thus, 511 g of a light yellow solid ofYGA2F was obtained with a yield of 76%.

Further, when a decomposition temperature (T_(d)) of the thus obtainedYGA2F was measured by a thermo-gravimetric/differential thermal analyzer(TG/DTA 320, manufactured by Seiko Instruments Inc.), the T_(d) was 500°C. or more, and it was understood that YGA2F has high T_(d).

In addition, the glass transition point was measured by a differentialscanning calorimeter (DSC, manufactured by PerkinElmer, Inc., Pyris 1).First, a sample was heated up to 400° C. at 40° C./min, and then it wascooled down to room temperature at 40° C./min. After that, thetemperature was raised to 400° C. at 10° C./min and then lowered to roomtemperature at 10° C./min, thereby obtaining the DSC chart shown in FIG.22. In FIG. 22, the X axis shows temperature and the Y axis shows heatflow. The Y axis shows endothermin an upward direction. It wasunderstood from this chart that the glass transition point (T_(g)) ofYGA2F was 150° C., and moreover that the aromatic amine compound of thepresent invention has excellent heat resistance.

FIG. 23 shows an absorption spectrum of a toluene solution of YGA2F.Moreover, FIG. 24 shows an absorption spectrum of a thin film of YGA2F.The measurement was conducted by using a UV-visible spectrophotometer(V-550, manufactured by Japan Spectroscopy Corporation). The solutionwas put in a quartz cell, and the thin film was evaporated on a quartzsubstrate to form the samples. Their absorption spectra from each ofwhich the absorption spectrum of quartz is subtracted are shown in FIGS.23 and 24. In FIGS. 23 and 24, the horizontal axis shows a wavelength(nm) while the vertical axis shows absorption intensity (arbitraryunit). In the case of the toluene solution, absorption was observed ataround 327 nm and 377 nm, and in the case of the thin film, it wasobserved at around 383 nm. The light emission spectrum of the toluenesolution of YGA2F (excitation wavelength: 340 nm) is shown in FIG. 25,while that of the thin film of YGA2F (excitation wavelength: 383 nm) isshown in FIG. 26. In FIGS. 25 and 26, the horizontal axis shows awavelength (nm) and the vertical axis shows light emission intensity(arbitrary unit). The peak of the light emission spectrum was observedat 400 nm and 422 nm in the case of the toluene solution (excitationwavelength: 340 nm), and 410 nm, 430 nm, and 537 nm in the case of thethin film (excitation wavelength: 383 mm).

In addition, the HOMO level of YGA2F in the thin film state was −5.27eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of YGA2F in FIG. 24. When the absorption edge was estimated asan optical energy gap, the energy gap was 3.05 eV. Therefore, the LUMOlevel was −2.22 eV.

Moreover, the oxidation reaction characteristic of YGA2F was measured bycyclic voltammetry (CV) measurement. Further, an electrochemicalanalyzer (ALS model 600A, manufactured by BAS Inc.) was used for themeasurement.

As for a solution used in the CV measurement, dehydrateddimethylformamide (DMF, manufactured by Aldrich, 99.8%, catalog number:22705-6) was used as a solvent. Tetra-n-butylammonium perchlorate(n-Bu₄NClO₄, manufactured by Tokyo Chemical Industry Co., Ltd., catalognumber: T0836), which was a supporting electrolyte, was dissolved in thesolvent such that the concentration of the tetra-n-butylammoniumperchlorate was 100 mmol/L. Moreover, the object to be measured wasdissolved such that the concentration thereof was set to be 1 mmol/L.Further, a platinum electrode (a PTE platinum electrode, manufactured byBAS Inc.) was used as a work electrode. A platinum electrode (a VC-3 Ptcounter electrode (5 cm), manufactured by BAS Inc.) was used as anauxiliary electrode. An Ag/Ag⁺ electrode (an RE5 nonaqueous solventreference electrode, manufactured by BAS Inc.) was used as a referenceelectrode. It is to be noted that the measurement was conducted at roomtemperature.

The oxidation reaction characteristic of YGA2F was measured as follows.A scan for changing the potential of the work electrode with respect tothe reference electrode from 1.0 V to −0.31 V after changing thepotential from −0.31 V to 1.0 V was set as one cycle, and 100 cycleswere measured. Further, the scanning speed of the CV measurement was setto be 0.1 V/s.

A result of the measurement on the oxidation reaction characteristic ofYGA2F is shown in FIG. 27, in which the horizontal axis shows thepotential (V) of the work electrode with respect to the referenceelectrode, while the vertical axis shows a value (μA) of current flowingbetween the work electrode and the auxiliary electrode.

In FIG. 27, a current indicating oxidation was observed at around 0.40 V(vs. Ag/Ag⁺ electrode). Regardless of the repetition of 100-cycle scans,the peak position and the peak intensity at the CV curve hardly changesin the oxidation reaction. Based on this fact, it was understood thatthe aromatic amine compound of the present invention is quite stableagainst the oxidation reaction and the subsequent reduction reaction(that is, repetition of oxidation).

Embodiment 4

This embodiment will explain a method of synthesizingN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: YGABP) expressed by Structure Formula (102). Synthesis Scheme(D-4) is shown below.

In a three-necked flask of 200 mL content, 2.0 g (5.0 mmol) of4,4-diiodo-1,1′-biphenyl, 3.3 g (10.0 mmol) of4-(carbazol-9-yl)diphenylamine, 65 mg (0.1 mmol) ofbis(dibenzylideneacetone)palladium(0), and 2.0 g (21.0 mmol) oftert-butoxysodium were put and nitrogen substitution was carried out.Then, 50 mL of toluene and 0.1 mL of tri(tert-butyl)phosphine (10 wt %hexane solution) were added and stirred for six hours at 80° C. Afterthe reaction mixture was cooled down to room temperature, the mixturewas filtered through celite, Florisil, and alumina. The filtrate wasthen washed with water or saturated saline. The mixture was washednaturally and magnesium sulfate was removed. The filtrate wasconcentrated to obtain a white solid, which was then recrystallized bychloroform and hexane; thus, 1.8 g of a white powder-like solid, whichis a target matter, was obtained with a yield of 45%. It was confirmedthat this compound wasN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: YGABP) expressed by Structure Formula (102).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz,DMSO-d₆): δ=7.12-7.17 (m, 2H), 7.20-7.30 (m, 16H), 7.38-7.47 (m, 12H),7.52 (d. J=8.7 Hz, 4H), 7.67 (d, J=9.0 Hz, 4H), and 8.22 (d, J=7.8 Hz,4H). A ¹H-NMR chart is also shown in FIGS. 28A and 28B. Further, FIG.28B is a chart showing an enlarged part in the range of 6.0 ppm to 9.0ppm of FIG. 28A.

The obtained YGABP1 with an amount of 1.8 g was then purified bysublimation for 15 hours at 300° C. under 7.8 Pa in the flow of argongas at a rate of 3.0 mL/min; thus, 1.6 g of a light yellow solid ofYGABP was obtained with a yield of 89%.

Further, when a decomposition temperature (T_(d)) of the thus obtainedYGABP was measured by a thermo-gravimetric/differential thermal analyzer(TG/DTA 320, manufactured by Seiko Instruments Inc.), the T_(d) was 500°C. or more, and it was understood that YGABP has high T_(d).

In addition, the glass transition point was measured by a differentialscanning calorimeter (DSC, manufactured by PerkinElmer, Inc., Pyris 1).First, a sample was heated up to 350° C. at 40° C./min, and then it wascooled down to room temperature at 40° C./min. After that, thetemperature was raised to 350° C. at 10° C./min and then lowered to roomtemperature at 10° C./min, thereby obtaining the DSC chart shown in FIG.29. In FIG. 29, the X axis shows temperature and the Y axis shows heatflow. The Y axis shows endothermin an upward direction. It wasunderstood from this chart that the glass transition point (T_(g)) ofYGABP was 144° C., and moreover that the aromatic amine compound of thepresent invention has excellent heat resistance.

FIG. 30 shows an absorption spectrum of a toluene solution of YGABP.FIG. 31 shows an absorption spectrum of a thin film of YGABP. Themeasurement was conducted by using a UV-visible spectrophotometer(V-550, manufactured by Japan Spectroscopy Corporation). The solutionwas put in a quartz cell, and the thin film was evaporated on a quartzsubstrate to form the samples. Their absorption spectra from each ofwhich the absorption spectrum of quartz is subtracted are shown in FIGS.30 and 31. In FIGS. 30 and 31, the horizontal axis shows a wavelength(nm) while the vertical axis shows absorption intensity (arbitraryunit). In the case of the toluene solution, absorption was observed ataround 328 nm and 346 nm, and in the case of the thin film, it wasobserved at around 349 nm. The light emission spectrum of the toluenesolution of YGABP (excitation wavelength: 350 nm) is shown in FIG. 32,while that of the thin film of YGABP (excitation wavelength: 350 nm) isshown in FIG. 33. In FIGS. 32 and 33, the horizontal axis shows awavelength (nm) and the vertical axis shows light emission intensity(arbitrary unit). The maximum light emission wavelength was 400 nm inthe case of the toluene solution (excitation wavelength: 350 nm), and410 nm in the case of the thin film (excitation wavelength: 350 nm).

In addition, the HOMO level of YGABP in the thin film state was −5.41eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of YGABP in FIG. 31. When the absorption edge was estimated asan optical energy gap, the energy gap was 3.13 eV. Therefore, the LUMOlevel was −2.28 eV.

Moreover, the oxidation reaction characteristic of YGABP was measured bycyclic voltammetry (CV) measurement. Further, an electrochemicalanalyzer (ALS model 600A, manufactured by BAS Inc.) was used for themeasurement.

As for a solution used in the CV measurement, dehydrateddimethylformamide (DMF, manufactured by Aldrich, 99.8%, catalog number:22705-6) was used as a solvent. Tetra-n-butylammonium perchlorate(n-Bu₄NClO₄, manufactured by Tokyo Chemical Industry Co., Ltd., catalognumber: T0836), which was a supporting electrolyte, was dissolved in thesolvent such that the concentration of the tetra-n-butylammoniumperchlorate was 100 mmol/L. Moreover, the object to be measured wasdissolved such that the concentration thereof was set to be 1 mmol/L.Further, a platinum electrode (a PTE platinum electrode, manufactured byBAS Inc.) was used as a work electrode. A platinum electrode (a VC-3 Ptcounter electrode (5 cm), manufactured by BAS Inc.) was used as anauxiliary electrode. An Ag/Ag⁺ electrode (an RE5 nonaqueous solventreference electrode, manufactured by BAS Inc.) was used as a referenceelectrode. It is to be noted that the measurement was conducted at roomtemperature.

The oxidation reaction characteristic of YGABP was measured as follows.A scan for changing the potential of the work electrode with respect tothe reference electrode from 1.0 V to −0.2 V after changing thepotential from −0.2 V to 1.0 V was set as one cycle, and 100 cycles weremeasured. Further, the scanning speed of the CV measurement was set tobe 0.1 V/s.

A result of the measurement on the oxidation reaction characteristic ofYGABP is shown in FIG. 34, in which the horizontal axis shows thepotential (V) of the work electrode with respect to the referenceelectrode, while the vertical axis shows a value (μA) of current flowingbetween the work electrode and the auxiliary electrode.

In FIG. 34, a current indicating oxidation was observed at around 0.66 V(vs. Ag/Ag⁺ electrode). Regardless of the repetition of 100-cycle scans,the peak position and the peak intensity at the CV curve hardly changesin the oxidation reaction. Based on this fact, it was understood thatthe aromatic amine compound of the present invention is quite stableagainst the oxidation reaction and the subsequent reduction reaction(that is, repetition of oxidation).

Embodiment 5

This embodiment will explain a light-emitting element of the presentinvention with reference to FIG. 35. A chemical formula of a materialused in this embodiment is shown below.

(Light-Emitting Element 1)

First, indium tin oxide including silicon oxide was formed over a glasssubstrate 2101 by a sputtering method, thereby forming a first electrode2102. The first electrode 2102 has a film thickness of 110 nm and anelectrode area of 2 mm×2 mm.

Next, the substrate over which the first electrode was formed was fixedto a substrate holder provided in a vacuum evaporation apparatus in sucha way that a surface of the substrate having the first electrode faceddownward. The pressure was reduced to be about 10⁻⁴ Pa and then, NPB andmolybdenum oxide (VI) were co-evaporated on the first electrode 2102,thereby forming a layer 2103 containing a composite material of anorganic compound and an inorganic compound. The film thickness of thelayer 2103 was 50 nm, and the weight ratio between NPB and molybdenumoxide (VI) was set 4:1 (=NPB: molybdenum oxide). It is to be noted thatthe co-evaporation method is an evaporation method in which evaporationis performed from plural evaporation sources in one process chamber.

Subsequently, a hole-transporting layer 2104 was formed in 10 nm thickover the layer 2103 containing a composite material by usingN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine(abbr.: YGAF) expressed by Structure Formula (21) by an evaporationmethod using resistance heating.

Further, a light-emitting layer 2105 of 30 nm thick was formed over thehole-transporting layer 2104 by co-evaporating9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbr.: CZPA) and9-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-10-phenylanthracene(abbr.: YGAPA). Here, the weight ratio between CzPA and YGAPA wasadjusted so as to be 1:0.04 (=CzPA: YGAPA).

After that, an electron-transporting layer 2106 was formed in 10 nmthick using tris(8-quinolinolato)aluminum (abbr.: Alq) over thelight-emitting layer 2105 by an evaporation method using resistanceheating.

Moreover, an electron-injecting layer 2107 was formed in 20 nm thick byco-evaporating Alq and lithium over the electron-transporting layer2106. Here, the weight ratio between Alq and lithium was adjusted so asto be 1:0.01 (=Alq: lithium).

Then, a second electrode 2108 was formed of aluminum in 200 nm thickover the electron-injecting layer 2107 by an evaporation method usingresistance heating. Thus, the light-emitting element 1 was manufactured.

(Light-Emitting Element 2)

The hole-transporting layer 2104 was formed in 10 nm thick byN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenyl-9,9-dimethylfluorene-2,7-diamine(abbr.: YGA2F) expressed by Structure Formula (71). The structure otherthan the hole-transporting layer is similar to that of thelight-emitting element 1.

(Light-Emitting Element 3)

The hole-transporting layer 2104 was formed in 10 nm thick byN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: YGABP) expressed by Structure Formula (102). The structure otherthan the hole-transporting layer is similar to that of thelight-emitting element 1.

(Comparative Light-Emitting Element 4)

The hole-transporting layer 2104 was formed of NPB in 10 nm thick. Thestructure other than the hole-transporting layer is similar to that ofthe light-emitting element 1.

FIG. 36 shows a current density-luminance characteristic of thelight-emitting elements 1 to 3 and the comparative light-emittingelement 4. FIG. 37 shows a voltage-luminance characteristic thereof, andFIG. 38 shows luminance-current efficiency characteristics thereof. Ascan be seen from FIG. 38, the light-emitting element using the aromaticamine compound of the present invention shows high current efficiency.Moreover, as shown in FIG. 37, a voltage necessary to obtain a certainluminance can be reduced in the light-emitting element of the presentinvention. That is to say, the drive voltage can be reduced. Therefore,the power consumption of the light-emitting element can be reduced.

In this way, the light-emitting element with the use of the aromaticamine compound of the present invention for the hole-transporting layercan have favorable characteristics.

Embodiment 6

This embodiment will explain a light-emitting element of the presentinvention with reference to FIG. 35. A chemical formula of a materialused in this embodiment is shown below.

(Light-Emitting Element 5)

First, indium tin oxide including silicon oxide was formed over theglass substrate 2101 by a sputtering method, thereby forming the firstelectrode 2102. The first electrode 2102 has a film thickness of 110 nmand an electrode area of 2 mm×2 mm.

Next, the substrate over which the first electrode was formed was fixedto a substrate holder provided in a vacuum evaporation apparatus in sucha way that a surface of the substrate having the first electrode faceddownward. The pressure was reduced to be about 10⁻⁴ Pa and then, NPB andmolybdenum oxide (VI) were co-evaporated on the first electrode 2102,thereby forming the layer 2103 containing a composite material of anorganic compound and an inorganic compound. The film thickness of thelayer 2103 was 50 nm, and the weight ratio between NPB and molybdenumoxide (VI) was set 4:1 (=NPB: molybdenum oxide). It is to be noted thatthe co-evaporation method is an evaporation method in which evaporationis performed from plural evaporation sources in one process chamber.

Subsequently, the hole-transporting layer 2104 was formed in 10 nm thickover the layer 2103 containing a composite material by usingN-[4-(carbazol-9-yl)phenyl]-N-phenyl-9,9-dimethylfluorenyl-2-amine(abbr.: YGAF) expressed by Structure Formula (21) by an evaporationmethod using resistance heating.

Further, the light-emitting layer 2105 of 30 nm thick was formed overthe hole-transporting layer 2104 by co-evaporating2-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-5-phenyl-1,3,4-oxadiazole(abbr.: YGAO11) and bis(2-phenylpyridinato)iridium(III)acetylacetonate(abbr.: Ir(ppy)₂(acac)). Here, the weight ratio between YGAO11 andIr(ppy)₂(acac) was adjusted so as to be 1:0.05 (=YGAO11:Ir(ppy)₂(acac)).

After that, the electron-transporting layer 2106 was formed in 10 nmthick using bis(2-methyl-8-quinolinolato)(4-phenylphenolato)aluminum(abbr.: BAlq) over the light-emitting layer 2105 by an evaporationmethod using resistance heating.

Moreover, the electron-injecting layer 2107 was formed in 20 nm thick byco-evaporating Alq and lithium over the electron-transporting layer2106. Here, the weight ratio between Alq and lithium was adjusted so asto be 1:0.01 (=Alq: lithium).

Then, the second electrode 2108 was formed of aluminum in 200 nm thickover the electron-injecting layer 2107 by an evaporation method usingresistance heating. Thus, the light-emitting element 5 was manufactured.

(Comparative Light-Emitting Element 6)

The hole-transporting layer 2104 was formed of NPB in 10 nm thick. Thestructure other than the hole-transporting layer is similar to that ofthe light-emitting element 5.

FIG. 39 shows a current density-luminance characteristic of thelight-emitting element 5 and the comparative light-emitting element 6.FIG. 40 shows a voltage-luminance characteristic thereof, and FIG. 41shows luminance-current efficiency characteristics thereof. As can beseen from FIG. 41, the light-emitting element using the aromatic aminecompound of the present invention shows high current efficiency. Asshown in FIG. 40, the light-emitting element of the present inventionhas almost the same drive voltage as the comparative light-emittingelement 6.

In addition, the triplet-excitation energy (energy gap) of each of YGAFand YGA1BP, which are the aromatic amine compounds of the presentinvention, and NPB used for the comparative light-emitting element 6 wascalculated. The calculation was performed in such a way that an optimalmolecular structure thereof in a ground state was calculated withB3LYP/6-311 (d, p) of density functional theory (DFT). The accuracy ofcalculation of the DFT is higher than that of Hartree-Fock (HF) whichdoes not consider electron correlation. In addition, the calculationcost of the DFT is lower than that of a method of perturbation (MP)which has the same level accuracy of calculation as the DFT. Therefore,the DFT was employed in the present calculation. The calculation wasperformed using a high-performance computer (HPC) (manufactured by SGIJapan, Ltd., Altix3700 DX). After that, the triplet-excitation energy(energy gap) of each of these compounds was calculated with theapplication of B3LYP/6-311 (d, p) of a time-dependent density functionaltheory (TDDFT) for the molecular structure whose structure was optimizedby the DFT. Further, the corresponding wavelength was calculated fromthe triplet-excitation energy (energy gap). The results are shown inTable 1 and FIG. 42.

TABLE 1 wavelength corresponding to material triplet-excitation energy(eV) triplet-excitation energy (nm) NPB 2.48 501 YGA1BP 2.87 432 YGAF2.70 458

As can be seen from Table 1 and FIG. 42, YGAF and YGA1BP which are thearomatic amine compounds of the present invention have highertriplet-excitation energy than NPB used for the comparativelight-emitting element 6. In particular, YGA1BP has hightriplet-excitation energy. The wavelength corresponding to thetriplet-excitation energy of the aromatic amine compound of the presentinvention is about 450 nm, which corresponds to blue color. On the otherhand, the wavelength corresponding to the triplet-excitation energy ofNPB used for the comparative light-emitting element 6 is 500 nm, whichcorresponds to green color. Therefore, in a case of using NPB for alayer which is in contact with a green phosphorescent material, evenwhen the green phosphorescent material is excited, the energy maytransfer to NPB. Accordingly, light is not emitted from thephosphorescent material, which lowers the luminous efficiency. Incontrast, in a case of using the aromatic amine compound of the presentinvention for a layer which is in contact with a phosphorescent materialemitting green phosphorescent light, the energy does not transfer fromthe excited green phosphorescent material to the aromatic amine compoundof the present invention. Moreover, when the aromatic amine compound ofthe present invention is excited, the energy can transfer to the greenphosphorescent material. Therefore, high luminous efficiency can beachieved.

Moreover, singlet-excitation energy is higher than triplet-excitationenergy. Therefore, a similar effect can also be obtained from afluorescent material as well as the phosphorescent material.Specifically, since the wavelength for the aromatic amine compound ofthe present invention with respect to the triplet-excitation energycorresponds to blue color, the wavelength corresponding to thesinglet-excitation energy is shorter than that of blue color. Therefore,in a case of using the aromatic amine compound for a layer which is incontact with a blue fluorescent material, the energy does not transferfrom the excited blue fluorescent material to the aromatic aminecompound of the present invention. In a case of the aromatic aminecompound of the present invention being excited, the energy can transferto the fluorescent material. Accordingly, high luminous efficiency canbe achieved.

In this manner, with the aromatic amine compound of the presentinvention used for the hole-transporting layer, the light-emittingelement with favorable characteristics can be obtained.

Embodiment 7

Embodiment 7 will explain a method of synthesizing4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP)expressed by Structure Formula (69). The following shows SynthesisScheme (J-1) of mYGA1BP.

In a three-necked flask of 200 mL content, 1.9 g (5.8 mmol) of4-(N-carbazolyl)diphenylamine and 2.0 g (21 mmol) of sodiumtert-butoxide were put and nitrogen substitution in the flask wascarried out. In this mixture, 30 mL of toluene, 0.1 mL oftri(tert-butyl)phosphine (10 wt % hexane solution), and 1.4 g (5.8 mmol)of 3-bromobiphenyl were added. The mixture was stirred under lowpressure so as to be deaerated. After the deaeration, 33 mg (0.06 mmol)of bis(dibenzylideneacetone)palladium(0) was added. This mixture wasstirred for five hours at 80° C. After the reaction, the reactionmixture was subjected to suction filtration through Florisil, celite,and alumina and the filtrate was concentrated, thereby obtaining a whitesolid. When this solid was recrystallized by dichloromethane and hexane,2.1 g of a white powder-like solid, which is a target matter, wasobtained with a yield of 98%. It was confirmed by nuclear magneticresonance spectroscopy (NMR) that this compound was4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP)expressed by Structure Formula (69).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz, CDCl₃):δ=7.07-7.12 (m, 1H), 7.17-7.20 (m, 1H), 7.27-7.47 (m, 20H), 7.53-7.56(m, 2H), and 8.14 (d, J=7.8 Hz, 2H). A ¹H-NMR chart is also shown inFIGS. 46A and 46B. Further, FIG. 46B is a chart showing an enlarged partin the range of 6.5 ppm to 8.5 ppm of FIG. 46A.

The obtained mYGA1BP with an amount of 1.9 g was purified by sublimationfor 15 hours at a heating temperature of 225° C. under a pressure of 5.9Pa in the flow of argon gas at a flow rate of 3.0 mL/min; thus, 1.7 g ofa white (achromatous) needle-like crystal as a target matter wasobtained with a yield of 90%.

A thermogravimetry-differential thermal analysis (TG-DTA) of mYGA1BP wasconducted by using a high vacuum differential type differential thermalbalance (manufactured by Bruker AXS K.K., DTA2410SA). When themeasurement was conducted under a low pressure of 10 Pa, the temperatureat which the weight becomes 95% or lower of the weight at the start ofthe measurement was 224° C. from the relation between the weight andtemperature (thermogravimetry). When the measurement was conducted atnormal pressure, the temperature at which the weight becomes 95% orlower of the weight at the start of the measurement was 391° C. It is tobe noted that the temperature-rising speed was 10° C./min in eithermeasurement.

FIG. 47 shows an absorption spectrum of a toluene solution of mYGA1BP.FIG. 48 shows an absorption spectrum of a thin film of mYGA1BP. Themeasurement was conducted by using a UV-visible spectrophotometer(V-550, manufactured by Japan Spectroscopy Corporation). The solutionwas put in a quartz cell, and the thin film was evaporated on a quartzsubstrate to form the samples. Their absorption spectra from each ofwhich the absorption spectrum of quartz is subtracted are shown in FIGS.47 and 48. In FIGS. 47 and 48, the horizontal axis shows a wavelength(nm) while the vertical axis shows absorption intensity (arbitraryunit). In the case of the toluene solution, absorption was observed ataround 294 nm and 313 nm, and in the case of the thin film, it wasobserved at around 317 nm. The light emission spectrum of the toluenesolution of mYGA1BP (excitation wavelength: 350 nm) is shown in FIG. 49,while that of the thin film of mYGA1BP (excitation wavelength: 317 nm)is shown in FIG. 50. In FIGS. 49 and 50, the horizontal axis shows awavelength (nm) and the vertical axis shows light emission intensity(arbitrary unit). The peak of the light emission spectrum was observedat 392 nm in the case of the toluene solution (excitation wavelength:350 nm), and 402 nm in the case of the thin film (excitation wavelength:317 nm).

In addition, the HOMO level of mYGA1BP in the thin film state was −5.57eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of mYGA1BP in FIG. 48. When the absorption edge was estimatedas an optical energy gap, the energy gap was 3.45 eV. Therefore, theLUMO level was −2.12 eV.

Embodiment 8

Embodiment 8 will explain a method of synthesizing4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP)expressed by Structure Formula (70). The following shows SynthesisScheme (K-1) of oYGA1BP.

In a three-necked flask of 200 mL content, 1.9 g (5.8 mmol) of4-(N-carbazolyl)diphenylamine and 2.0 g (21 mmol) of sodiumtert-butoxide were put and nitrogen substitution in the flask wascarried out. In this mixture, 30 mL of toluene, 0.1 mL oftri(tert-butyl)phosphine (10 wt % hexane solution), and 1.4 g (5.8 mmol)of 2-bromobiphenyl were added. The mixture was stirred under lowpressure so as to be deaerated. After the deaeration, 33 mg (0.06 mmol)of bis(dibenzylideneacetone)palladium(0) was added. This mixture wasstirred for five hours at 80° C. After the reaction, the reactionmixture was subjected to suction filtration through Florisil, celite,and alumina and the filtrate was concentrated, thereby obtaining a whitesolid. When this solid was recrystallized by dichloromethane and hexane,2.3 g of a white powder-like solid as a target matter was obtained witha yield of 82%. It was confirmed by nuclear magnetic resonancespectroscopy (NMR) that this compound was4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP)expressed by Structure Formula (70).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz, CDCl₃);δ=6.91-6.96 (m, 3H), 7.06-7.09 (m, 2H), 7.12 (d, 8.7 Hz, 2H), 7.18-7.44(m, 17H), and 8.10-8.13 (m, 2H). A ¹H-NMR chart is also shown in FIGS.51A and 51B. Further, FIG. 51B is a chart showing an enlarged part inthe range of 6.5 ppm to 8.5 ppm of FIG. 51A.

The obtained oYGA1BP with an amount of 2.0 g was purified by sublimationfor 15 hours at a heating temperature of 210° C. under a pressure of 5.9Pa in the flow of argon gas at a flow rate of 3.0 mL/min; thus, 1.9 g ofa white (achromatous) needle-like crystal as a target matter wasobtained with a yield of 87%.

A thermogravimetry-differential thermal analysis (TG-DTA) of oYGA1BP wasconducted by using a high vacuum differential type differential thermalbalance (manufactured by Bruker AXS K.K., DTA2410SA). When themeasurement was conducted under a low pressure of 10 Pa, the temperatureat which the weight becomes 95% or lower of the weight at the start ofthe measurement was 208° C. from the relation between the weight andtemperature (thermogravimetry). When the measurement was conducted atnormal pressure, the temperature at which the weight becomes 95% orlower of the weight at the start of the measurement was 370° C. It is tobe noted that the temperature-rising speed was 10° C./min in eithermeasurement.

FIG. 52 shows an absorption spectrum of a toluene solution of oYGA1BP.FIG. 53 shows an absorption spectrum of a thin film of oYGA1BP. Themeasurement was conducted by using a UV-visible spectrophotometer(V-550, manufactured by Japan Spectroscopy Corporation). The solutionwas put in a quartz cell, and the thin film was evaporated on a quartzsubstrate to form the samples. Their absorption spectra from each ofwhich the absorption spectrum of quartz is subtracted are shown in FIGS.52 and 53. In FIGS. 52 and 53, the horizontal axis shows a wavelength(nm) while the vertical axis shows absorption intensity (arbitraryunit). In the case of the toluene solution, absorption was observed ataround 294 nm and 311 nm, and in the case of the thin film, it wasobserved at around 317 nm. The light emission spectrum of the toluenesolution of oYGA1BP (excitation wavelength: 350 nm) is shown in FIG. 54,while that of the thin film of oYGA1BP (excitation wavelength: 317 nm)is shown in FIG. 55. In FIGS. 54 and 55, the horizontal axis shows awavelength (nm) and the vertical axis shows light emission intensity(arbitrary unit). The peak of the light emission spectrum was observedat 404 nm in the case of the toluene solution (excitation wavelength:350 nm), and 407 nm in the case of the thin film (excitation wavelength:317 nm).

In addition, the HOMO level of oYGA1BP in the thin film state was −5.56eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of oYGA1BP in FIG. 53. When the absorption edge was estimatedas an optical energy gap, the energy gap was 3.46 eV. Therefore, theLUMO level was −2.10 eV.

Embodiment 9

Embodiment 9 will explain a method of synthesizingN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP) expressed by Structure Formula (107).

[Step 1]

A method of synthesizing N,N′-di(1-naphthyl)benzidine is explained. Thefollowing shows Synthesis Scheme (L-1) of N,N′-di(1-naphthyl)benzidine.

In a three-necked flask of 500 mL content, 20 g (50 mmol) of4,4′-diiodobiphenyl, 14 g (100 mmol) of 1-naphthylamine, 580 mg (1 mmol)of bis(dibenzylideneacetone)palladium(0), and 12 g (12 mmol) of sodiumtert-butoxide were put and 100 mL of dehydrated toluene was added. Then,the pressure in the three-necked flask was reduced for three minutes toperform deaeration until no bubbles came out. In this mixture, 6.0 mL(3.0 mmol) of tri(tert-butyl)phosphine (10 wt % hexane solution) wasadded and stirred while heated at 100° C. in a nitrogen atmosphere. Theheating was stopped after three hours, and about 700 mL of a mixturesolution of hot toluene and ethyl acetate was added to this reactionsuspension and the suspension was filtered through Florisil, alumina,and celite. The obtained filtrate was washed with water and dried byadding magnesium sulfate to an organic layer. This suspension wasfurther filtered and the obtained filtrate was concentrated. Afteradding hexane to this concentrated solution, recrystallization wasperformed by applying ultrasonic waves. The produced solid was filteredoff and dried. Thus, 13 g of a white powder-like target matter wasobtained with a yield of 57%. An Rf value of the target matter by asilicagel thin layer chromatography (TLC) (developing solution washexane: ethyl acetate=2:1) was 0.53 and that of 1-naphthylamine was0.36.

[Step 2]

A method of synthesizingN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP) is explained. The following shows Synthesis Scheme (L-2)of YGNBP.

In a three-necked flask of 100 mL content, 3.5 g (11 mmol) of4-bromophenylcarbazole, 2.2 g (5.0 mmol) ofN,N′-di(1-naphthyl)benzidine, 30 mg (0.1 mmol) ofbis(dibenzylideneacetone)palladium(0), and 1.5 g (15 mmol) of sodiumtert-butoxide were put, and 20 mL of dehydrated xylene was added. Then,the pressure in the three-necked flask was reduced for three minutes toperform deaeration until no bubbles came out. In this mixture, 0.6 mL(0.3 mmol) of tri(tert-butyl)phosphine (10 wt % hexane solution) wasadded and stirred while heated at 130° C. in a nitrogen atmosphere. Theheating was stopped after four hours, and about 200 mL of toluene wasadded to this reaction suspension and filtration was performed throughFlorisil, alumina, and celite. The obtained filtrate was washed withwater and dried by adding magnesium sulfate to an organic layer. Thissuspension was further filtered through Florisil, alumina, and celite,and the obtained filtrate was concentrated. After adding acetone andhexane to this concentrated solution, recrystallization was performed byapplying ultrasonic waves. The produced solid was filtered off anddried. Thus, 2.0 g of a light-yellow powder as a target matter wasobtained with a yield of 43%. It was confirmed by nuclear magneticresonance spectroscopy (NMR) that this compound wasN,N′-bis[4-(carbazol-9-yl)phenyl]-N,N′-di(1-naphthyl)biphenyl-4,4′-diamine(abbr.: YGNBP) expressed by Structure Formula (107).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz, CDCl₃):δ (ppm)=7.19-7.58 (m, 36H), 7.84 (d, J=7.8, 2H), 7.93 (d, J=7.8, 2H),8.05 (d, J=8.1, 2H), and 8.12 (d, J=7.2, 4H). A ¹H-NMR chart is alsoshown in FIGS. 56A and 56B. Further, FIG. 56B is a chart showing anenlarged part in the range of 6.0 ppm to 9.0 ppm of FIG. 56A.

Moreover, the ¹³C-NMR data on this compound are shown. The ¹³C-NMR (75.5MHz, CDCl₃): δ (ppm)=109.82, 119.65, 120.23, 122.06, 122.47, 123.15,124.10, 125.78, 126.34, 126.45, 126.69, 126.99, 127.36, 127.47, 127.86,128.55, 130.69, 131.26, 134.41, 135.40, 141.12, 143.02, 146.85, 147.53.A ¹³C-NMR chart is also shown in FIGS. 57A and 57B. Further, FIG. 57B isa chart showing an enlarged part in the range of 100 ppm to 160 ppm ofFIG. 57A.

A thermogravimetry-differential thermal analysis (TG-DTA) of YGNBP wasconducted by using a high vacuum differential type differential thermalbalance (manufactured by Bruker AXS K.K., DTA2410SA). When themeasurement was conducted under a low pressure of 10 Pa, the temperatureat which the weight becomes 95% or lower of the weight at the start ofthe measurement was 390° C. from the relation between the weight andtemperature (thermogravimetry). When the measurement was conducted atnormal pressure, the weight was 99% of the weight at the start of themeasurement at 500° C., and the heat resistance was excellent. It is tobe noted that the temperature-rising speed was 10° C./min in eithermeasurement.

In addition, the glass transition point of YGNBP was measured by adifferential scanning calorimeter (DSC, manufactured by PerkinElmer,Inc., Pyris 1). As shown in a DSC chart of FIG. 72, the temperature wasraised to 500° C. at 10° C./min. In FIG. 72, the X axis showstemperature and the Y axis shows heat flow. The Y axis shows endothermin an upward direction. It was understood from this chart that the glasstransition point (T_(g)) of YGNBP was as high as 171° C.

FIG. 58 shows an absorption spectrum of a toluene solution of YGNBP andan absorption spectrum of a thin film of YGNBP. The measurement wasconducted by using a UV-visible spectrophotometer (V-550, manufacturedby Japan Spectroscopy Corporation). The solution was put in a quartzcell, and the thin film was evaporated on a quartz substrate to form thesamples. Their absorption spectra from each of which the absorptionspectrum of quartz is subtracted are shown in FIG. 58. In FIG. 58, thehorizontal axis shows a wavelength (nm) while the vertical axis showsabsorption intensity (arbitrary unit). In the case of the toluenesolution, absorption was observed at around 345 nm, and in the case ofthe thin film, it was observed at around 349 nm. The light emissionspectrum of the toluene solution of YGNBP (excitation wavelength: 350nm) and that of the thin film of YGNBP (excitation wavelength: 349 nm)are shown in FIG. 59. In FIG. 59, the horizontal axis shows a wavelength(nm) and the vertical axis shows light emission intensity (arbitraryunit). The peak of the light emission spectrum was observed at 435 nm inthe case of the toluene solution (excitation wavelength: 350 nm), and526 nm in the case of the thin film (excitation wavelength: 349 nm).

In addition, the HOMO level of YGNBP in the thin film state was −5.34eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of YGNBP in FIG. 58. When the absorption edge was estimated asan optical energy gap, the energy gap was 3.19 eV. Therefore, the LUMOlevel was −2.15 eV.

Embodiment 10

Embodiment 10 will explain a method of synthesizingN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP) expressed by Structure Formula (115).

[Step 1]

A method of synthesizing 9-(4-bromo-1-naphthyl)carbazole will beexplained. The following shows Synthesis Scheme (M-1) of9-(4-bromo-1-naphthyl)carbazole.

In a three-necked flask of 300 mL content, 14 g (50 mmol) of1,4-dibromonaphthalene, 6.7 g (40 mmol) of carbazole, 1.9 g (10 mmol) ofcopper iodide(I), 1.3 g (5.0 mmol) of 18-crown-6-ether, 10 g (72 mmol)of potassium carbonate, and 8 mL of1,3-dimethyl-3,4,5,6-tetrahydro-2(1H)-pyrimidinone (abbr.: DMPU) wereput and heated at 170° C. for about 30 hours in a nitrogen atmosphere.After this reaction suspension was cooled down to room temperature, 300mL of hot toluene was added to this reaction suspension and filtrationwas performed through celite. The obtained filtrate was washed withwater, dilute hydrochloric acid, water, a sodium hydrogen carbonateaqueous solution, and water in this order, and dried by adding magnesiumsulfate to an organic layer. This suspension was filtered throughFlorisil and celite, and the obtained filtrate was concentrated. Thisconcentrated solution was sorted by silicagel chromatography (toluene:hexane=1:1). Thus, 7.5 g of a white powder as a target matter wasobtained with a yield of 50%. It was confirmed by nuclear magneticresonance spectroscopy (NMR) that this compound was9-(4-bromo-1-naphthyl)carbazole.

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz, CDCl₃):δ (ppm)=6.93-6.96 (m, 2H), 7.25-7.33 (m, 6H), 7.45 (d, J=7.8, 1H), 7.60(t, J=6.9, 1H), 7.94 (d, J=7.8, 1H), 8.16-8.19 (m, 2H), and 8.38 (d,J=8.7, 1H). A ¹H-NMR chart is also shown in FIGS. 60A and 60B. Further,FIG. 60B is a chart showing an enlarged part in the range of 6.0 ppm to9.0 ppm of FIG. 60A.

[Step 2]

A method of synthesizingN,N′-bis[4-(carbazol-9-yl)naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP) will be explained. The following shows Synthesis Scheme(M-2) of CNABP.

In a three-necked flask of 100 mL content, 3.4 g (9 mmol) of9-(4-bromo-1-naphthyl)carbazole, 1.4 g (4 mmol) ofN,N′-diphenylbenzidine, 60 mg (0.1 mmol) ofbis(dibenzylideneacetone)palladium(0), and 1.5 g (15 mmol) of sodiumtert-butoxide were put, and 20 mL of dehydrated xylene was added. Then,the pressure in the three-necked flask was reduced for three minutes toperform deaeration until no bubbles came out. In this mixture, 0.6 mL(0.3 mmol) of tri(tert-butyl)phosphine (10 wt % hexane solution) wasadded and stirred while heated at 120° C. in a nitrogen atmosphere. Theheating was stopped after four hours, and about 200 mL of toluene wasadded to this reaction suspension and filtration was performed throughFlorisil, alumina, and celite. The obtained filtrate was washed withwater and dried by addition of magnesium sulfate. This suspension wasfurther filtered through Florisil, alumina, and celite, and the obtainedfiltrate was concentrated. After adding acetone and hexane to thisconcentrated filtrate, recrystallization was performed by applyingultrasonic waves. The produced solid was filtered off and dried. Thus,2.7 g of a light-yellow powder as a target matter was obtained with ayield of 73%. It was confirmed by nuclear magnetic resonancespectroscopy (NMR) that this compound wasN,N′-bis[4-(carbazol-9-yl)naphthyl]-N,N′-diphenylbiphenyl-4,4′-diamine(abbr.: CNABP) expressed by Structure Formula (115).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz, CDCl₃):δ (ppm)=7.03 (t, J=7.2, 2H), 7.09 (d, J=7.8, 4H), 7.15-7.19 (m, 8H),7.25-7.43 (m, 18H), 7.48-7.53 (m, 6H), 7.63 (d, J=7.8, 2H), 8.12 (d,J=8.4, 2H), and 8.22 (d, J=6.9, 4H). A ¹H-NMR chart is also shown inFIGS. 61A and 61B. Further, FIG. 61B is a chart showing an enlarged partin the range of 6.0 ppm to 9.0 ppm of FIG. 61A.

A thermogravimetry-differential thermal analysis (TG-DTA) of CNABP wasconducted by using a high vacuum differential type differential thermalbalance (manufactured by Bruker AXS K.K., DTA2410SA). When themeasurement was conducted under a low pressure of 10 Pa, the temperatureat which the weight becomes 95% or lower of the weight at the start ofthe measurement was 380° C. from the relation between the weight andtemperature (thermogravimetry). When the measurement was conducted atnormal pressure, the weight was 94% of the weight at the start of themeasurement at 500° C., and the heat resistance was excellent. It is tobe noted that the temperature-rising speed was 10° C./min in eithermeasurement.

In addition, the glass transition point of CNABP was measured by adifferential scanning calorimeter (DSC, manufactured by PerkinElmer,Inc., Pyris 1). As shown in a DSC chart of FIG. 73, the temperature wasraised to 500° C. at 10° C./min. In FIG. 73, the X axis showstemperature and the Y axis shows heat flow. The Y axis shows endothermin an upward direction. It was understood from this chart that the glasstransition point (T_(g)) of CNABP was as high as 183° C.

FIG. 62 shows an absorption spectrum of a toluene solution of CNABP andan absorption spectrum of a thin film of CNABP. The measurement wasconducted by using a UV-visible spectrophotometer (V-550, manufacturedby Japan Spectroscopy Corporation). The solution was put in a quartzcell, and the thin film was evaporated on a quartz substrate to form thesamples. Their absorption spectra from each of which the absorptionspectrum of quartz is subtracted are shown in FIG. 62. In FIG. 62, thehorizontal axis shows a wavelength (nm) while the vertical axis showsabsorption intensity (arbitrary unit). In the case of the toluenesolution, absorption was observed at around 338 nm and 380 nm, and inthe case of the thin film, it was observed at around 340 nm and 383 nm.The light emission spectrum of the toluene solution of CNABP (excitationwavelength: 340 nm) and that of the thin film of CNABP (excitationwavelength: 383 nm) are shown in FIG. 63. In FIG. 63, the horizontalaxis shows a wavelength (nm) and the vertical axis shows light emissionintensity (arbitrary unit). The peak of the light emission spectrum wasobserved at 455 nm in the case of the toluene solution (excitationwavelength: 340 nm), and 499 nm and 522 nm in the case of the thin film(excitation wavelength: 383 nm).

In addition, the HOMO level of CNABP in the thin film state was −5.43eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of CNABP in FIG. 62. When the absorption edge was estimated asan optical energy gap, the energy gap was 2.90 eV. Therefore, the LUMOlevel was −2.53 eV.

Embodiment 11

Embodiment 11 will explain a method of synthesizingN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-di-1-naphthylbiphenyl-4,4′-diamine(abbr.: CNNBP) expressed by Structure Formula (120). The following showsSynthesis Scheme (N-1) of CNNBP.

In a three-necked flask of 100 mL content, 3.4 g (9 mmol) of9-(4-bromo-1-naphthyl)carbazole, 1.8 g (4 mmol) ofN,N′-di(1-naphthyl)benzidine, 60 mg (0.1 mmol) ofbis(dibenzylideneacetone)palladium(0), and 1.5 g (15 mmol) of sodiumtert-butoxide were put, and 20 mL of dehydrated xylene was added. Then,the pressure in the three-necked flask was reduced for three minutes toperform deaeration until no bubbles came out. In this mixture, 0.6 mL(0.3 mmol) of tri(tert-butyl)phosphine (10 wt % hexane solution) wasadded and stirred while heated at 130° C. in a nitrogen atmosphere. Theheating was stopped after four hours, and about 200 mL of toluene wasadded to this reaction suspension and filtration was performed throughFlorisil, alumina, and celite. The obtained filtrate was washed withwater and dried by adding magnesium sulfate to an organic layer. Thissuspension was further filtered through Florisil, alumina, and celite,and the obtained filtrate was concentrated. After adding acetone andhexane to this concentrated filtrate, recrystallization was performed byapplying ultrasonic waves. The produced solid was filtered off anddried. Thus, 0.8 g of a light-yellow powder as a target matter wasobtained with a yield of 20%. It was confirmed by nuclear magneticresonance spectroscopy (NMR) that this compound wasN,N′-bis[4-(carbazol-9-yl)-1-naphthyl]-N,N′-di-1-naphthylbiphenyl-4,4′-diamine(abbr.: CNNBP).

The ¹H-NMR data on this compound are shown. The ¹H-NMR (300 MHz, CDCl₃):δ (ppm)=6.88 (d, J=8.1, 4H), 7.05 (d, J=7.8, 4H), 7.26-7.53 (m, 30H),7.76 (d, J=7.8, 2H), 7.92 (d, J=8.4, 2H), 8.14 (d, J=7.8, 2H), and8.19-8.23 (m, 6H). A ¹H-NMR chart is also shown in FIGS. 64A and 64B.Further, FIG. 64B is a chart showing an enlarged part in the range of6.0 ppm to 9.0 ppm of FIG. 64A.

A thermogravimetry-differential thermal analysis (TG-DTA) of CNNBP wasconducted by using a high vacuum differential type differential thermalbalance (manufactured by Bruker AXS K.K., DTA2410SA). When themeasurement was conducted under a low pressure of 10 Pa, the temperatureat which the weight becomes 95% or lower of the weight at the start ofthe measurement was 400° C. from the relation between the weight andtemperature (thermogravimetry). When the measurement was conducted atnormal pressure, the weight was 98% of the weight at the start of themeasurement at 500° C., and the heat resistance was excellent. It is tobe noted that the temperature-rising speed was 10° C./min in eithermeasurement.

In addition, the glass transition point of CNNBP was measured by adifferential scanning calorimeter (DSC, manufactured by PerkinElmer,Inc., Pyris 1). As shown in a DSC chart of FIG. 74, the temperature wasraised to 500° C. at 10° C./min. In FIG. 74, the X axis showstemperature and the Y axis shows heat flow. The Y axis shows endothermin an upward direction. It was understood from this chart that the glasstransition point (T_(g)) of CNNBP was as high as 213° C.

FIG. 65 shows an absorption spectrum of a toluene solution of CNNBP andan absorption spectrum of a thin film of CNNBP. The measurement wasconducted by using a UV-visible spectrophotometer (V-550, manufacturedby Japan Spectroscopy Corporation). The solution was put in a quartzcell, and the thin film was evaporated on a quartz substrate to form thesamples. Their absorption spectra from each of which the absorptionspectrum of quartz is subtracted are shown in FIG. 65. In FIG. 65, thehorizontal axis shows a wavelength (nm) while the vertical axis showsabsorption intensity (arbitrary unit). In the case of the toluenesolution, absorption was observed at around 370 nm, and in the case ofthe thin film, it was observed at around 374 nm. The light emissionspectrum of the toluene solution of CNNBP (excitation wavelength: 370nm) and that of the thin film of CNNBP (excitation wavelength: 374 nm)are shown in FIG. 66. In FIG. 66, the horizontal axis shows a wavelength(nm) and the vertical axis shows light emission intensity (arbitraryunit). The peak of the light emission spectrum was observed at 450 nm inthe case of the toluene solution (excitation wavelength: 370 nm), and545 nm in the case of the thin film (excitation wavelength: 374 nm).

In addition, the HOMO level of CNNBP in the thin film state was −5.45eV, which was measured by photoelectron spectrometer (AC-2, manufacturedby Riken Keiki Co., Ltd.) in the air. Moreover, the absorption edge wasobtained from Tauc plot using data on the absorption spectrum of thethin film of CNNBP in FIG. 65. When the absorption edge was estimated asan optical energy gap, the energy gap was 3.00 eV. Therefore, the LUMOlevel was −2.45 eV.

Embodiment 12

Embodiment 12 will explain a light-emitting element of the presentinvention with reference to FIG. 67. The following shows a chemicalformula of a material used in this embodiment.

(Light-Emitting Element 7)

First, indium tin oxide including silicon oxide was formed over a glasssubstrate 2201 by a sputtering method, thereby forming a first electrode2202. The first electrode 2202 has a thickness of 110 nm and anelectrode area of 2 mm×2 mm.

Next, the substrate over which the first electrode was formed was fixedto a substrate holder provided in a vacuum evaporation apparatus in sucha way that a surface of the substrate having the first electrode faceddownward. The pressure was reduced to be about 10⁻⁴ Pa and then, NPB andmolybdenum oxide (VI) were co-evaporated on the first electrode 2202,thereby forming a layer 2203 containing a composite material of anorganic compound and an inorganic compound. The film thickness of thelayer 2203 was 50 nm, and the weight ratio between NPB and molybdenumoxide (VI) was set 4:1 (=NPB: molybdenum oxide). It is to be noted thatthe co-evaporation method is an evaporation method in which evaporationis performed from plural evaporation sources in one process chamber.

Subsequently, a hole-transporting layer 2204 was formed in 10 nm thickover the layer 2203 containing a composite material by using4-(carbazol-9-yl)phenyl-4′-phenyltriphenylamine (abbr.: YGA1BP)expressed by Structure Formula (52) by an evaporation method usingresistance heating.

Further, a light-emitting layer 2205 of 30 nm thick was formed over thehole-transporting layer 2204 by co-evaporating9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbr.: CzPA) andN,N′-bis[4-(9H-carbazol-9-yl)phenyl]-N,N′-diphenylstylbene-4,4′-diamine(abbr.: YGA2S). Here, the weight ratio between CzPA and YGA2S wasadjusted so as to be 1:0.04 (=CzPA: YGA2S).

After that, a first electron-transporting layer 2206 a was formed of Alqin 20 nm thick over the light-emitting layer 2205 by an evaporationmethod using resistance heating.

Moreover, a second electron-transporting layer 2206 b was formed ofbathophenanthroline (abbr.: BPhen) in 10 nm thick over the firstelectron-transporting layer 2206 a by an evaporation method usingresistance heating.

Moreover, an electron-injecting layer 2207 was formed in 1 nm thick byevaporating lithium fluoride over the second electron-transporting layer2206 b by an evaporation method using resistance heating.

Lastly, a second electrode 2208 was formed of aluminum in 200 nm thickover the electron-injecting layer 2207 by an evaporation method usingresistance heating. Thus, the light-emitting element 7 was manufactured.

(Light-Emitting Element 8)

As the hole-transporting layer 2204,4-(carbazol-9-yl)phenyl-2′-phenyltriphenylamine (abbr.: oYGA1BP)expressed by Structure Formula (70) was formed in 10 nm thick. Thestructure other than the hole-transporting layer is similar to that ofthe light-emitting element 7.

(Light-Emitting Element 9)

As the hole-transporting layer 2204,4-(carbazol-9-yl)phenyl-3′-phenyltriphenylamine (abbr.: mYGA1BP)expressed by Structure Formula (69) was formed in 10 nm thick. Thestructure other than the hole-transporting layer is similar to that ofthe light-emitting element 7.

(Comparative Light-Emitting Element 10)

As the hole-transporting layer 2204, NPB was formed in 10 nm thick. Thestructure other than the hole-transporting layer is similar to that ofthe light-emitting element 7.

FIG. 68 shows current density-luminance characteristics of thelight-emitting elements 7 to 9 and the comparative light-emittingelement 10. FIG. 69 shows voltage-luminance characteristics thereof, andFIG. 70 shows luminance-current efficiency characteristics thereof. Inaddition, FIG. 71 shows light emission spectra thereof when a current of1 mA flows.

As can be seen from FIG. 69, the light-emitting element using thearomatic amine compound of the present invention has high currentefficiency although the chromaticity coordinate thereof is similar tothat of the comparative light-emitting element 10. As shown in FIG. 68,the light-emitting element of the present invention has almost the samedrive voltage as the comparative light-emitting element 10. Therefore,by the use of the aromatic amine compound of the present invention, thelight-emitting element with high power efficiency and low powerconsumption can be obtained.

Specifically, the comparative light-emitting element 10 showed bluelight emission with its CIE chromaticity coordinate (x=0.16, y=0.17) ata luminance of 930 cd/m². At a luminance of 930 cd/m², the currentefficiency thereof was 3.9 cd/A, the voltage thereof was 4.8 V, thecurrent density thereof was 24 mA/cm², and the power efficiency thereofwas 2.61 m/W.

On the other hand, the light-emitting element 7 showed blue lightemission with its CIE chromaticity coordinate (x=0.16, y=0.17) at aluminance of 1090 cd/m². At a luminance of 1090 cd/m², the currentefficiency thereof was as high as 7.2 cd/A, the voltage thereof was 4.6V, the current density thereof was 15 mA/cm², and the power efficiencythereof was as high as 4.91 m/W.

The light-emitting element 8 showed blue light emission with its CIEchromaticity coordinate (x=0.16, y=0.17) at a luminance of 930 cd/m². Ata luminance of 930 cd/m², the current efficiency thereof was as high as7.6 cd/A, the voltage thereof was 4.6 V, the current density thereof was12 mA/cm², and the power efficiency thereof was as high as 5.21 m/W.

The light-emitting element 9 showed blue light emission. At a luminanceof 930 cd/m², the current efficiency thereof was as high as 7.4 cd/A,the voltage thereof was 4.8 V, the current density thereof was 13mA/cm², and the power efficiency thereof was as high as 4.81 m/W.

As thus described, YGA1BP, which is the aromatic amine compound of thepresent invention, has higher triplet-excitation energy than NPB usedfor the comparative light-emitting element 10. In particular, YGA1BP hashigh triplet-excitation energy with an asymmetrical structure. Inaddition, the wavelength corresponding to the triplet-excitation energyof the aromatic amine compound of the present invention is about 450 nm,which corresponds to blue color. On the other hand, the wavelengthcorresponding to the triplet-excitation energy of NPB used for thecomparative light-emitting element 10 is about 500 nm, which correspondsto green color. Moreover, the singlet-excitation energy is higher thanthe triplet-excitation energy. In other words, since the wavelengthcorresponding to the triplet-excitation energy of the aromatic aminecompound of the present invention corresponds to blue color, thewavelength corresponding to the singlet-excitation energy is shorterthan the wavelength of blue color. Therefore, when the aromatic aminecompound is used for a layer which is in contact with a blue fluorescentmaterial, the energy does not transfer from the excited blue fluorescentmaterial to the aromatic amine compound of the present invention.Moreover, when the aromatic amine compound of the present invention isexcited, the energy can transfer to the fluorescent material. Thus, highluminous efficiency can be realized.

In this manner, by the use of the aromatic amine compound of the presentinvention for the hole-transporting layer, the light-emitting elementwith favorable characteristics can be obtained.

Embodiment 13

This embodiment will explain the material used in another embodiment.

[Synthesis Example of YGAO11]

Described hereinafter is a method of synthesizing2-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-5-phenyl-1,3,4-oxadiazole(abbr.: YGAO11) expressed by Structure Formula (201).

[Step 1]

Synthesis of 2-(4-bromophenyl)-5-phenyl-1,3,4-oxadiazole (abbr.: O11Br)is explained. In Step 1, O11Br was synthesized in accordance with thefollowing procedure (i) to (iii).

(i) Synthesis of 4-bromobenzohydrazide.

First, 3.0 g (13.9 mmol) of methyl-4-bromobenzoate was put in a 100-mLthree-necked flask, 10 mL of ethanol was added therein, and the mixturewas stirred. Thereafter, 4.0 mL of hydrazine monohydrate was addedtherein, and the mixture was heated and stirred at 78° C. for fivehours. The obtained solid was washed with water and collected by suctionfiltration; thus, 2.0 g of a white solid of 4-bromobenzohydrazide as atarget matter was obtained (yield: 67%).

(ii) Synthesis of 1-benzoyl-2-(4-bromobenzoyl)hydrazine.

Subsequently, 2.0 g (13.9 mmol) of the 4-bromobenzohydrazide obtained in(i) above was put in a 300-mL three-necked flask, 7 mL ofN-methyl-2-pyrrolidone (abbr.: NMP) was added therein, and then themixture was stirred. Thereafter, a mixture of 2.5 mL ofN-methyl-2-pyrrolidone and 2.5 mL (21.5 mmol) of benzoyl chloride wasdropped through a 50-mL dropping funnel, and the mixture was stirred at80° C. for three hours. The obtained solid was washed with water and asodium carbonate aqueous solution in this order and collected by suctionfiltration. Then, the solid was recrystallized with acetone; thus, 3.6 gof a white solid of 1-benzoyl-2-(4-bromobenzoyl)hydrazine as a targetmatter was obtained (yield: 80%).

(iii) Synthesis of O11Br

Further, 15 g (47 mmol) of the 1-benzoyl-2-(4-bromobenzoyl)hydrazineobtained by the method shown in (ii) above was put in a 200-mLthree-necked flask, 100 mL of phosphoryl chloride was added therein, andthe mixture was heated and stirred at 100° C. for five hours. After thereaction, the solid obtained by completely distilling off phosphorylchloride was washed with water and a sodium carbonate aqueous solutionin this order and collected by suction filtration. Then, the solid wasrecrystallized with methanol; thus, 13 g of a white solid of O11Br as atarget matter of Step 1 was obtained (yield: 89%). A synthesis scheme ofStep 1 described above is shown in the following scheme (E-1).

[Step 2]

Synthesis of2-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-5-phenyl-1,3,4-oxadiazole(abbr.: YGAO11)

In a 100-mL three-necked flask, 3.0 g (10.0 mmol) of O11Br obtained inStep 1, 3.4 g (10.0 mmol) of YGA obtained in Step 1 of Embodiment 1, and1.9 g (19.9 mmol) of sodium tert-butoxide were put, and nitrogensubstitution was carried out. Then, 45 mL of toluene, 0.3 mL of a 10%hexane solution of tri(tert-butyl)phosphine, and 0.3 g (0.6 mmol) ofbis(dibenzylideneacetone)palladium(0) were added therein, and themixture was heated and stirred at 120° C. for five hours. After thereaction, the mixture was filtered through Celite, and the filtrate waswashed with water and then dried with magnesium sulfate. After beingdried, the solution was filtrated, and the filtrate was concentrated.The obtained solid was dissolved in toluene and purified by silica gelcolumn chromatography. Purification by column chromatography wasperformed by using toluene as a developing solvent and then using amixed solvent of toluene: ethyl acetate=1:1 as a developing solvent. Thepurified solid was recrystallized with chloroform and hexane; thus, 4.7g of a light-yellow solid YGAO11 as a target matter of this synthesisexample was obtained with a yield of 85%. The following scheme (E-2)shows the synthesis scheme of Step 3 in the above description.

The following shows a result of analyzing YGAO11 that was obtained bynuclear magnetic resonance spectroscopy (¹H-NMR). FIG. 43A shows a¹H-NMR chart and FIG. 43B shows an enlarged chart thereof.

¹H-NMR (300 MHz, CDCl₃): δ=7.14-7.53 (m, 19H), δ=8.03 (d, J=8.7, 2H),δ=8.11-8.15 (m, 4H).

[Synthesis Example of YGAPA]

Described hereinafter is a method of synthesizing9-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-10-phenylanthracene(abbr.: YGAPA) expressed by Structure Formula (202).

[Step 1]

A method of synthesizing 9-phenyl-10-(4-bromophenyl)anthracene (abbr.:PA) will be explained.

(i) Synthesis of 9-phenylanthracene

The following shows Synthesis Scheme (F-1) of 9-phenylanthracene.

First, 5.4 g (21.1 mmol) of 9-bromoanthracene, 2.6 g (21.1 mmol) ofphenylboronic acid, 60 mg (0.21 mmol) of palladium acetate (Pd(OAc)₂),10 mL (20 mmol) of a potassium carbonate (K₂CO₃) aqueous solution (2mol/L), 263 mg (0.84 mmol) of tri(o-tolyl)phosphine (P(o-tolyl)₃), and20 mL of 1,2-dimethoxyethane (abbr.: DME) were mixed and stirred at 80°C. for nine hours. After the reaction, the precipitated solid wascollected by suction filtration, dissolved in toluene, and filteredthrough Florisil, Celite, and alumina. The filtrate was washed withwater and saturated saline and then dried with magnesium sulfate. Afterthe solution was filtered naturally and the filtrate was concentrated,21.5 g of a light-brown solid of 9-phenylanthracene as a target matterwas obtained with a yield of 85%.

(ii) Synthesis of 10-bromo-9-phenylanthracene.

The following shows Synthesis Scheme (F-2) of10-bromo-9-phenylanthracene.

After 6.0 g (23.7 mmol) of 9-phenylanthracene was dissolved in 80 mL ofcarbon tetrachloride, a solution of 3.80 g (21.1 mmol) of brominedissolved in 10 mL of carbon tetrachloride was dropped through adropping funnel into the reaction solution. After the dropping, thesolution was stirred at room temperature for one hour. After thereaction, a sodium thiosulfate aqueous solution was added to stop thereaction. An organic layer was washed with a sodium hydroxide (NaOH)aqueous solution and saturated saline and dried with magnesium sulfate.After the solution was filtered naturally, the filtrate wasconcentrated, dissolved in toluene, and filtered through Florisil,Celite, and alumina. When the filtrate was concentrated andrecrystallized with dichloromethane and hexane, 7.0 g of a light-yellowsolid of 10-bromo-9-phenylanthracene, which is a target matter, wasobtained with a yield of 89%.

(iii) Synthesis of 9-iodo-10-phenylanthracene.

The following shows Synthesis Scheme (F-3) of9-iodo-10-phenylanthracene.

After 3.33 g (10 mmol) of 9-bromo-10-phenylanthracene was dissolved in80 mL of tetrahydrofuran (abbreviation: THF) and cooled to −78° C., 7.5mL (12.0 mmol) of n-BuLi (1.6 mol/L) was dropped through a droppingfunnel into the reaction solution, and the mixture was stirred for onehour. Subsequently, a solution of 5 g (20.0 mmol) of iodine dissolved in20 mL of THF was dropped, and the solution was further stirred at −78°C. for two hours. After the reaction, a sodium thiosulfate aqueoussolution was added to stop the reaction. An organic layer was washedwith a sodium thiosulfate aqueous solution and saturated saline anddried with magnesium sulfate. After the solution was filtered naturally,the filtrate was concentrated and recrystallized with ethanol; thus, 3.1g of a light-yellow solid of 9-iodo-10-phenylanthracene as a targetmatter was obtained with a yield of 83%.

(iv) Synthesis of 9-phenyl-10-(4-bromophenyl)anthracene (abbreviation:PA).

The following shows Synthesis Scheme (F-4) of9-phenyl-10-(4-bromophenyl)anthracene (abbreviation: PA).

First, 1.0 g (2.63 mmol) of 9-iodo-10-phenylanthracene, 542 mg (2.70mmol) of p-bromophenylboronic acid, 46 mg (0.03 mmol) oftetrakis(triphenylphosphine)palladium(0) (Pd(PPh₃)₄), 3 mL (6 mmol) of apotassium carbonate (K₂CO₃) aqueous solution (2 mol/L), and 10 mL oftoluene were mixed and stirred at 80° C. for nine hours. After thereaction, toluene was added therein, and the mixture was filteredthrough Florisil, Celite, and alumina. The filtrate was washed withwater and saturated saline and then dried with magnesium sulfate. Afterthe solution was filtered naturally, the filtrate was concentrated andrecrystallized with chloroform and hexane; thus, 562 mg of a light-brownsolid of 9-phenyl-10-(4-bromophenyl)anthracene as a target matter wasobtained with a yield of 45%.

[Step 2]

A method of synthesizing9-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-10-phenylanthracene(abbreviation: YGAPA) will be explained. The following shows SynthesisScheme (F-5) of YGAPA.

First, 409 mg (1.0 mmol) of 9-phenyl-10-(4-bromophenyl)anthracene, 339mg (1.0 mmol) of YGA obtained in Step 1 of Embodiment 1, 6 mg (0.01mmol) of bis(dibenzylideneacetone)palladium(0), 500 mg (5.2 mmol) ofsodium tert-butoxide, 0.1 mL of tri(tert-butyl)phosphine (10 wt % hexanesolution), and 10 mL of toluene were mixed and stirred at 80° C. forfour hours. After the reaction, the reaction solution was washed withwater, a water layer was extracted with toluene, and the water layertogether with an organic layer was washed with saturated saline and thendried with magnesium sulfate. After the solution was filtered naturallyand concentrated, the obtained oil-like substance was purified by silicagel column chromatography (hexane toluene=7:3) and recrystallized withdichloromethane and hexane. Then, 534 mg of a yellow powder-like solidof YGAPA as a target matter was obtained with a yield of 81%. When thiscompound was measured by nuclear magnetic resonance spectrometry (NMR),it was confirmed that the compound was9-(4-{N-[4-(carbazol-9-yl)phenyl]-N-phenylamino}phenyl)-10-phenylanthracene(abbreviation: YGAPA). FIGS. 44A and 44B show ¹H-NMR charts of YGAPA.

[Synthesis Example of CzPA]

A method of synthesizing 9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene(abbr.: CzPA) expressed by Structure Formula (203) is explained.

The following shows Synthesis Scheme (H-1) of9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbr.: CzPA).

A mixture of 1.3 g (3.2 mmol) of 9-phenyl-10-(4-bromophenyl)anthracene,578 mg (3.5 mmol) of carbazole, 50 mg (0.10 mmol) ofbis(dibenzylideneacetone)palladium(0), 1.0 g (10 mmol) oftert-butoxysodium, 0.1 mL of tri(tert-butyl)phosphine (10 wt % hexanesolution), and 30 mL of toluene was heated to reflux at 110° C. for 10hours. After the reaction, the reaction solution was washed with water,a water layer was extracted with toluene, and the water layer togetherwith an organic layer was washed with saturated saline and then driedwith magnesium sulfate. After the solution was filtered naturally andconcentrated, the obtained oil-like substance was purified by silica gelcolumn chromatography (hexane: toluene=7:3) and recrystallized withdichloromethane and hexane. Then, 1.5 g of9-[4-(N-carbazolyl)]phenyl-10-phenylanthracene (abbreviation: CzPA) as atarget matter was obtained with a yield of 93%.

The NMR data on the obtained CzPA is shown. ¹H-NMR (300 MHz, CDCl₃):δ=8.22 (d, J=7.8 Hz, 2H), 7.86-7.82 (m, 3H), and 7.61-7.36 (m, 20H). Inaddition, FIG. 45 shows a ¹H-NMR chart.

When 5.50 g of the obtained CzPA was sublimed and purified for 20 hoursunder the conditions of a temperature at 270° C., in argon flow (flowrate: 3.0 mL/min), and a pressure of 6.7 Pa, 3.98 g of CzPa wascollected with a yield of 72%.

This application is based on Japanese Patent Application serial no.2006-077631 filed in Japan Patent Office on March 20, in 2006, theentire contents of which are hereby incorporated by reference.

1. An aromatic amine compound expressed by General Formula (1)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; Ar¹ represents an aryl group having 6 to 25 carbon atoms; and αrepresents a substituent expressed by any of General Formulae (1-2) to(1-4), in which R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent ahydrogen atom or an alkyl group having 1 to 4 carbon atoms.
 2. Alight-emitting element comprising: a light emitting layer and thearomatic amine compound according to claim 1 between a pair ofelectrodes.
 3. A light-emitting element comprising: a light-emittinglayer and a layer containing the aromatic amine compound according toclaim 1, between a pair of electrodes, wherein the layer containing thearomatic amine compound is in contact with the light-emitting layer. 4.A light-emitting element comprising: a light-emitting layer and thearomatic amine compound according to claim 1, between a pair ofelectrodes, wherein the aromatic amine compound is included in thelight-emitting layer.
 5. The light-emitting element according to claim2, wherein the light-emitting layer contains a phosphorescent materialwhich emits phosphorescent light.
 6. The light-emitting elementaccording to claim 5, wherein the phosphorescent material emits greenlight.
 7. The light-emitting element according to claim 2, wherein thelight-emitting layer contains a fluorescent material which emitsfluorescent light.
 8. The light-emitting element according to claim 7,wherein the fluorescent material emits blue light.
 9. A light-emittingdevice comprising: the light-emitting element according to claim 2; anda controller for controlling light emission of the light-emittingelement.
 10. An electronic appliance comprising a display portion,wherein the display portion is provided with the light-emitting elementaccording to claim 2 and a controller for controlling light emission ofthe light-emitting element.
 11. An aromatic amine compound expressed byGeneral Formula (2)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; A¹ represents an arylene group having 6 to 25 carbonatoms; Ar¹ represents an aryl group having 6 to 25 carbon atoms; and αrepresents a substituent expressed by General Formula (2-1), in whichR⁵¹ and R⁵² each represent any of a hydrogen atom, an alkyl group having1 to 4 carbon atoms, and an aryl group having 6 to 12 carbon atoms; andR⁵³ to R⁵⁸ each represent a hydrogen atom or an alkyl group having 1 to4 carbon atoms.
 12. A light-emitting element comprising: a lightemitting layer and the aromatic amine compound according to claim 11between a pair of electrodes.
 13. A light-emitting element comprising: alight-emitting layer and a layer containing the aromatic amine compoundaccording to claim 11, between a pair of electrodes, wherein the layercontaining the aromatic amine compound is in contact with thelight-emitting layer.
 14. A light-emitting element comprising: alight-emitting layer and the aromatic amine compound according to claim11, between a pair of electrodes, wherein the aromatic amine compound isincluded in the light-emitting layer.
 15. The light-emitting elementaccording to claim 12, wherein the light-emitting layer contains aphosphorescent material which emits phosphorescent light.
 16. Thelight-emitting element according to claim 15, wherein the phosphorescentmaterial emits green light.
 17. The light-emitting element according toclaim 12, wherein the light-emitting layer contains a fluorescentmaterial which emits fluorescent light.
 18. The light-emitting elementaccording to claim 17, wherein the fluorescent material emits bluelight.
 19. A light-emitting device comprising: the light-emittingelement according to claim 12; and a controller for controlling lightemission of the light-emitting element.
 20. An electronic appliancecomprising a display portion, wherein the display portion is providedwith the light-emitting element according to claim 12 and a controllerfor controlling light emission of the light-emitting element.
 21. Anaromatic amine compound expressed by General Formula (3)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; Ar¹ represents an aryl group having 6 to 25 carbonatoms; and α represents a substituent expressed by any of GeneralFormulae (3-2) to (3-4), in which R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹each represent a hydrogen atom or an alkyl group having 1 to 4 carbonatoms.
 22. A light-emitting element comprising: a light emitting layerand the aromatic amine compound according to claim 21 between a pair ofelectrodes.
 23. A light-emitting element comprising: a light-emittinglayer and a layer containing the aromatic amine compound according toclaim 21, between a pair of electrodes, wherein the layer containing thearomatic amine compound is in contact with the light-emitting layer. 24.A light-emitting element comprising: a light-emitting layer and thearomatic amine compound according to claim 21, between a pair ofelectrodes, wherein the aromatic amine compound is included in thelight-emitting layer.
 25. The light-emitting element according to claim22, wherein the light-emitting layer contains a phosphorescent materialwhich emits phosphorescent light.
 26. The light-emitting elementaccording to claim 25, wherein the phosphorescent material emits greenlight.
 27. The light-emitting element according to claim 22, wherein thelight-emitting layer contains a fluorescent material which emitsfluorescent light.
 28. The light-emitting element according to claim 27,wherein the fluorescent material emits blue light.
 29. A light-emittingdevice comprising: the light-emitting element according to claim 22; anda controller for controlling light emission of the light-emittingelement.
 30. An electronic appliance comprising a display portion,wherein the display portion is provided with the light-emitting elementaccording to claim 22 and a controller for controlling light emission ofthe light-emitting element.
 31. An aromatic amine compound expressed byGeneral Formula (4)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; Ar¹ represents an aryl group having 6 to 25 carbonatoms; and α represents a substituent expressed by General Formula(4-1), in which R⁵¹ and R⁵² each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to 12carbon atoms; and R⁵³ to R⁵⁸ each represent a hydrogen atom or an alkylgroup having 1 to 4 carbon atoms.
 32. A light-emitting elementcomprising: a light emitting layer and the aromatic amine compoundaccording to claim 31 between a pair of electrodes.
 33. A light-emittingelement comprising: a light-emitting layer and a layer containing thearomatic amine compound according to claim 31, between a pair ofelectrodes, wherein the layer containing the aromatic amine compound isin contact with the light-emitting layer.
 34. A light-emitting elementcomprising: a light-emitting layer and the aromatic amine compoundaccording to claim 31, between a pair of electrodes, wherein thearomatic amine compound is included in the light-emitting layer.
 35. Thelight-emitting element according to claim 32, wherein the light-emittinglayer contains a phosphorescent material which emits phosphorescentlight.
 36. The light-emitting element according to claim 35, wherein thephosphorescent material emits green light.
 37. The light-emittingelement according to claim 32, wherein the light-emitting layer containsa fluorescent material which emits fluorescent light.
 38. Thelight-emitting element according to claim 37, wherein the fluorescentmaterial emits blue light.
 39. A light-emitting device comprising: thelight-emitting element according to claim 32; and a controller forcontrolling light emission of the light-emitting element.
 40. Anelectronic appliance comprising a display portion, wherein the displayportion is provided with the light-emitting element according to claim32 and a controller for controlling light emission of the light-emittingelement.
 41. An aromatic amine compound expressed by General Formula (5)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; R³ to R⁷ each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and a phenyl group; and αrepresents a substituent expressed by any of General Formulae (5-2) to(5-4), in which R²¹ to R²⁹, R³¹ to R³⁹, and R⁴¹ to R⁴⁹ each represent ahydrogen atom or an alkyl group having 1 to 4 carbon atoms.
 42. Alight-emitting element comprising: a light emitting layer and thearomatic amine compound according to claim 41 between a pair ofelectrodes.
 43. A light-emitting element comprising: a light-emittinglayer and a layer containing the aromatic amine compound according toclaim 41, between a pair of electrodes, wherein the layer containing thearomatic amine compound is in contact with the light-emitting layer. 44.A light-emitting element comprising: a light-emitting layer and thearomatic amine compound according to claim 41, between a pair ofelectrodes, wherein the aromatic amine compound is included in thelight-emitting layer.
 45. The light-emitting element according to claim42, wherein the light-emitting layer contains a phosphorescent materialwhich emits phosphorescent light.
 46. The light-emitting elementaccording to claim 45, wherein the phosphorescent material emits greenlight.
 47. The light-emitting element according to claim 42, wherein thelight-emitting layer contains a fluorescent material which emitsfluorescent light.
 48. The light-emitting element according to claim 47,wherein the fluorescent material emits blue light.
 49. A light-emittingdevice comprising: the light-emitting element according to claim 42; anda controller for controlling light emission of the light-emittingelement.
 50. An electronic appliance comprising a display portion,wherein the display portion is provided with the light-emitting elementaccording to claim 42 and a controller for controlling light emission ofthe light-emitting element.
 51. An aromatic amine compound expressed byGeneral Formula (6)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; R³ to R⁷ each represent any of a hydrogen atom, analkyl group having 1 to 4 carbon atoms, and a phenyl group; and αrepresents a substituent expressed by General Formula (6-1), in whichR⁵¹ and R⁵² each represent any of a hydrogen atom, an alkyl group having1 to 4 carbon atoms, and an aryl group having 6 to 12 carbon atoms, andR⁵³ to R⁵⁸ each represent a hydrogen atom or an alkyl group having 1 to4 carbon atoms.
 52. A light-emitting element comprising: a lightemitting layer and the aromatic amine compound according to claim 51between a pair of electrodes.
 53. A light-emitting element comprising: alight-emitting layer and a layer containing the aromatic amine compoundaccording to claim 51, between a pair of electrodes, wherein the layercontaining the aromatic amine compound is in contact with thelight-emitting layer.
 54. A light-emitting element comprising: alight-emitting layer and the aromatic amine compound according to claim51, between a pair of electrodes, wherein the aromatic amine compound isincluded in the light-emitting layer.
 55. The light-emitting elementaccording to claim 52, wherein the light-emitting layer contains aphosphorescent material which emits phosphorescent light.
 56. Thelight-emitting element according to claim 55, wherein the phosphorescentmaterial emits green light.
 57. The light-emitting element according toclaim 52, wherein the light-emitting layer contains a fluorescentmaterial which emits fluorescent light.
 58. The light-emitting elementaccording to claim 57, wherein the fluorescent material emits bluelight.
 59. A light-emitting device comprising: the light-emittingelement according to claim 52; and a controller for controlling lightemission of the light-emitting element.
 60. An electronic appliancecomprising a display portion, wherein the display portion is providedwith the light-emitting element according to claim 52 and a controllerfor controlling light emission of the light-emitting element.
 61. Anaromatic amine compound expressed by General Formula (7)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; and α represents a substituent expressed by any ofGeneral Formulae (7-2) to (7-4), in which R²¹ to R²⁹, R³¹ to R³⁹, andR⁴¹ to R⁴⁹ each represent a hydrogen atom or an alkyl group having 1 to4 carbon atoms.
 62. A light-emitting element comprising: a lightemitting layer and the aromatic amine compound according to claim 61between a pair of electrodes.
 63. A light-emitting element comprising: alight-emitting layer and a layer containing the aromatic amine compoundaccording to claim 61, between a pair of electrodes, wherein the layercontaining the aromatic amine compound is in contact with thelight-emitting layer.
 64. A light-emitting element comprising: alight-emitting layer and the aromatic amine compound according to claim61, between a pair of electrodes, wherein the aromatic amine compound isincluded in the light-emitting layer.
 65. The light-emitting elementaccording to claim 62, wherein the light-emitting layer contains aphosphorescent material which emits phosphorescent light.
 66. Thelight-emitting element according to claim 65, wherein the phosphorescentmaterial emits green light.
 67. The light-emitting element according toclaim 62, wherein the light-emitting layer contains a fluorescentmaterial which emits fluorescent light.
 68. The light-emitting elementaccording to claim 67, wherein the fluorescent material emits bluelight.
 69. A light-emitting device comprising: the light-emittingelement according to claim 62; and a controller for controlling lightemission of the light-emitting element.
 70. An electronic appliancecomprising a display portion, wherein the display portion is providedwith the light-emitting element according to claim 62 and a controllerfor controlling light emission of the light-emitting element.
 71. Anaromatic amine compound expressed by General Formula (8),

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms; and α represents a substituent expressed by GeneralFormula (8-1), in which R⁵¹ and R⁵² each represent any of a hydrogenatom, an alkyl group having 1 to 4 carbon atoms, and an aryl grouphaving 6 to 12 carbon atoms, and R⁵³ to R⁵⁸ each represent a hydrogenatom or an alkyl group having 1 to 4 carbon atoms.
 72. A light-emittingelement comprising: a light emitting layer and the aromatic aminecompound according to claim 71 between a pair of electrodes.
 73. Alight-emitting element comprising: a light-emitting layer and a layercontaining the aromatic amine compound according to claim 71, between apair of electrodes, wherein the layer containing the aromatic aminecompound is in contact with the light-emitting layer.
 74. Alight-emitting element comprising: a light-emitting layer and thearomatic amine compound according to claim 71, between a pair ofelectrodes, wherein the aromatic amine compound is included in thelight-emitting layer.
 75. The light-emitting element according to claim72, wherein the light-emitting layer contains a phosphorescent materialwhich emits phosphorescent light.
 76. The light-emitting elementaccording to claim 75, wherein the phosphorescent material emits greenlight.
 77. The light-emitting element according to claim 72, wherein thelight-emitting layer contains a fluorescent material which emitsfluorescent light.
 78. The light-emitting element according to claim 77,wherein the fluorescent material emits blue light.
 79. A light-emittingdevice comprising: the light-emitting element according to claim 72; anda controller for controlling light emission of the light-emittingelement.
 80. An electronic appliance comprising a display portion,wherein the display portion is provided with the light-emitting elementaccording to claim 72 and a controller for controlling light emission ofthe light-emitting element.
 81. An aromatic amine compound expressed byGeneral Formula (10)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms, and R³⁰ represents a hydrogen atom or an alkyl grouphaving 1 to 4 carbon atoms.
 82. A light-emitting element comprising: alight emitting layer and the aromatic amine compound according to claim81 between a pair of electrodes.
 83. A light-emitting elementcomprising: a light-emitting layer and a layer containing the aromaticamine compound according to claim 81, between a pair of electrodes,wherein the layer containing the aromatic amine compound is in contactwith the light-emitting layer.
 84. A light-emitting element comprising:a light-emitting layer and the aromatic amine compound according toclaim 81, between a pair of electrodes, wherein the aromatic aminecompound is included in the light-emitting layer.
 85. The light-emittingelement according to claim 82, wherein the light-emitting layer containsa phosphorescent material which emits phosphorescent light.
 86. Thelight-emitting element according to claim 85, wherein the phosphorescentmaterial emits green light.
 87. The light-emitting element according toclaim 82, wherein the light-emitting layer contains a fluorescentmaterial which emits fluorescent light.
 88. The light-emitting elementaccording to claim 87, wherein the fluorescent material emits bluelight.
 89. A light-emitting device comprising: the light-emittingelement according to claim 82; and a controller for controlling lightemission of the light-emitting element.
 90. An electronic appliancecomprising a display portion, wherein the display portion is providedwith the light-emitting element according to claim 82 and a controllerfor controlling light emission of the light-emitting element.
 91. Anaromatic amine compound expressed by General Formula (11)

wherein in the formula, R¹ and R² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to25 carbon atoms, and R⁵¹ and R⁵² each represent any of a hydrogen atom,an alkyl group having 1 to 4 carbon atoms, and an aryl group having 6 to12 carbon atoms.
 92. A light-emitting element comprising: a lightemitting layer and the aromatic amine compound according to claim 91between a pair of electrodes.
 93. A light-emitting element comprising: alight-emitting layer and a layer containing the aromatic amine compoundaccording to claim 91, between a pair of electrodes, wherein the layercontaining the aromatic amine compound is in contact with thelight-emitting layer.
 94. A light-emitting element comprising: alight-emitting layer and the aromatic amine compound according to claim91, between a pair of electrodes, wherein the aromatic amine compound isincluded in the light-emitting layer.
 95. The light-emitting elementaccording to claim 92, wherein the light-emitting layer contains aphosphorescent material which emits phosphorescent light.
 96. Thelight-emitting element according to claim 95, wherein the phosphorescentmaterial emits green light.
 97. The light-emitting element according toclaim 92, wherein the light-emitting layer contains a fluorescentmaterial which emits fluorescent light.
 98. The light-emitting elementaccording to claim 97, wherein the fluorescent material emits bluelight.
 99. A light-emitting device comprising: the light-emittingelement according to claim 92; and a controller for controlling lightemission of the light-emitting element.
 100. An electronic appliancecomprising a display portion, wherein the display portion is providedwith the light-emitting element according to claim 92 and a controllerfor controlling light emission of the light-emitting element.